1、Designation: E1379 90 (Reapproved 2010)Standard Specification forLaboratory Glass Dewar Flask1This standard is issued under the fixed designation E1379; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A n
2、umber in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification provides standard material and per-formance requirements for glass Dewar flasks suitable forgeneral laboratory use.1.
3、2 The values stated in SI units are to be regarded asstandard. No other units of measurement are included in thisstandard.2. Referenced Documents2.1 ASTM Standards:2B85 Specification for Aluminum-Alloy Die CastingsE438 Specification for Glasses in Laboratory ApparatusE671 Specification for Maximum P
4、ermissible Thermal Re-sidual Stress in Annealed Glass Laboratory Apparatus3. Classification3.1 Glass Dewar flasks shall be of the following sizes: 265mL, 665 mL, 1000 mL, 1900 mL, 4300 mLNOTE 1The term millilitre (mL) is commonly used as a special namefor the cubic centimetre (cm3) and similarly the
5、 litre (L) for 1000 cubiccentimetres, in accordance with the International System of Units (SI).4. Material and Annealing4.1 Flasks shall be made of borosilicate glass conforming tothe requirement of Type I, Class A, Specification E438.4.2 Maximum residual thermal stress shall conform toSpecificatio
6、n E671.4.3 Aluminum base alloy metal shall conform to AlloyNumber A380 of Specification B85.5. Appearance5.1 The general appearance of the flasks shall conform toFig. 1.6. Design6.1 Flasks shall be cylindrically shaped and have doublewalls silvered on the inside. The space between the walls shallbe
7、evacuated to a vacuum level of 5 3 107Torr and sealed.Temperatures are to be held in excess of 500C duringevacuation.6.2 Flasks shall be firmly cemented into the base to protectthe sealing tip.6.3 Flasks shall have a protective plastic mesh, or shall becoated with a baked-on plastisol over exposed g
8、lass surface.7. Capacity and Dimensions7.1 Standard Dewar flasks for government use shall con-form to the requirements of Table 1.7.2 Other Dewar flasks (not found in Table 1) are approvedfor use if they meet all of the design criteria found in Section6.8. Keywords8.1 dewar; flasks; glass1This speci
9、fication is under the jurisdiction of ASTM Committee E41 onLaboratory Apparatus and is the direct responsibility of Subcommittee E41.01 onApparatus.Current edition approved Sept. 1, 2010. Published September 2010. Originallyapproved in 1990. Last previous edition approved in 2005 as E1379 90 (2005).
10、DOI: 10.1520/E1379-90R10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.TABLE 1 Capacity and Dimensions for
11、Glass Dewar FlasksNominalCapacity(mL)O.D. BodyNominal(mm)Overall HeightNominal(mm)I.D. BodyNominal(mm)Body DepthNominal(mm)265 75 152 60 113665 86 241 68 1951000 86 343 68 3021900 149 267 119 1954300 177 337 152 2761Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken,
12、 PA 19428-2959, United States.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof in
13、fringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this stan
14、dard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your v
15、iews known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contac
16、ting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).FIG. 1 Glass Dewar FlaskE1379 90 (2010)2