1、Designation: E 1794 03Standard Specification forAdhesive for Bonding Foam Cored Sandwich Panels (200FElevated Humidity Service), Type II Panels1This standard is issued under the fixed designation E 1794; the number immediately following the designation indicates the year oforiginal adoption or, in t
2、he case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 Thi
3、s specification covers two-part adhesives for bondingfoam core sandwich panels. The adhesive may be used for newproduction or depot maintenance. The adhesive should besuitable for forming bonds that can withstand long-termexposure to temperatures from 55 to 93C (67 to 200F)and also withstand combina
4、tions of stress, temperature, andhumidity expected to be encountered in service. The adhesivesshall be used for bonding aluminum alloy facing to foam core,inserts, edge attachments, and other components of a foamcored sandwich panel.1.2 The values stated in SI units are to be regarded as thestandard
5、 where only SI units are given or where SI units aregiven first followed by English units; where English units aregiven first followed by SI units, the English units are to beregarded as the standard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its
6、 use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:B 209 Specification for Aluminum and Aluminum-AlloySheet and Plate2D 1002
7、 Test Method forApparent Shear Strength of Single-Lap-Joint Adhesively Bonded Metal Specimens by Ten-sion Loading (Metal-to-Metal)3E 864 Practice for Surface Preparation of Aluminum Alloysto be Adhesively Bonded in Honeycomb Shelter Panels4E 1749 Terminology of Rigid Wall Relocatable Shelters42.2 Mi
8、litary Standard:MIL-STD-202F Test Methods for Electronic and ElectricalComponent Parts52.3 Federal Specification:QQ-A-250/11d Aluminum Alloy 6061T6, Plate and Sheet53. Terminology3.1 DefinitionsSee Terminology E 1749 for definitions ofterms used in this specification.3.2 Definitions of Terms Specifi
9、c to This Standard:3.2.1 adhesive lifethe maximum time that an adhesive,when mixed in a prescribed quantity can set at a designatedtemperature, after which the adhesive, when used to preparespecimens, will deliver the required properties.4. Requirements4.1 MaterialThe adhesive shall be a two-part th
10、ermoset-ting epoxy paste containing no asbestos and, when tested usingthe test methods described in Section 6, shall meet therequirements of Section 4. The adhesive shall not have adeleterious effect on the components being bonded over therange of temperatures at which the adhesive will be used.4.2
11、Working Characteristics:4.2.1 ApplicationThe adhesive shall be suitable for appli-cation to facings and foam core materials. The adhesive shallbe suitable for spray application to faying surfaces.4.2.2 CuringThe time, temperature, and pressure used tocure the adhesive shall be within the range speci
12、fied herein.4.2.2.1 Curing Time and TemperatureThe adhesive, whenmixed in accordance with the manufacturers instructions, shallmeet the requirements of this specification when cured at atemperature of not more than 99C (210F) for 60 min, or107C (225F) for 45 min. The timing of the cure shall startwh
13、en the panel skins have reached the specified temperature.The temperature for the cure shall be fully attained within 3 hafter the first application of the adhesive to the faying surface.4.2.2.2 Curing PressureSpecimens for testing under thisspecification shall be cured under a normal load of 50 6 1
14、4 kPa(8.0 6 1.0 psi). No more than2hat25C (77F) shall elapse1This specification is under the jurisdiction of ASTM Committee E06 onPerformance of Buildings and is the direct responsibility of Subcommittee E06.53on Materials and Processes for Durable Rigidwall Relocatable Structures.Current edition ap
15、proved April 10, 2003. Published May 2003. Originallyapproved in 1996. Last previous edition approved in 2000 as E 179400.2Annual Book of ASTM Standards, Vol 02.02.3Annual Book of ASTM Standards, Vol 15.06.4Annual Book of ASTM Standards, Vol 04.11.5Available from Standardization Documents Order Desk
16、, Bldg. 4 Section D, 700Robbins Ave., Philadelphia, PA 19111-5094, Attn: NPODS.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.between the application of the adhesive to the faying surfaceand the application of the pressure.4.2.3 Mix
17、 RatioThe mix ratio for the two parts of theadhesive shall be as defined by the manufacturer.4.3 Storage LifeThe storage life shall not exceed one yearfrom the date of manufacture, when the components of theadhesive are stored at a temperature between 10C (50F) and42C (90F). The adhesive shall be co
18、nsidered to have met thisstorage life requirement if all the characteristics described in4.1 and 4.5 are met by the adhesive after the one year storageperiod described above.4.4 Adhesive LifeThe adhesive life of one quart of themixed adhesive at 25C (77F) shall not be less than 120 min(2 h), at whic
19、h time the adhesive shall meet the requirements of4.5.4.5 Mechanical PropertiesThe minimum mechanicalproperties of the adhesives, when cured as specified, shall meetthe requirements of Table 1.5. Significance and Use5.1 This specification is intended to provide information onthe properties of adhesi
20、ves, and the test methods required toevaluate adhesives to be used in the production bonding ofaluminum alloys to foam core materials for the manufacture oftactical shelters.6. Test Methods6.1 Qualification TestsFor qualification, the adhesiveshall be tested using the tests described in this section
21、. Sheartests shall be performed in accordance with Test MethodD 1002 except that the length of the test coupon shall be 103.7mm (414 in.) and the thickness shall be 2.196 mm (0.090 in.).6.2 Preparation of Test Specimens Prepare at least tenspecimens for each separate test. The metal to be bonded sha
22、llbe 6061-T6 (Federal Specification QQ-A-250/11d or Specifi-cation B 209) and cleaned as specified in Practice E 864. Time,temperature, and pressure for curing the adhesive shall be asspecified in 5.3.2.1 and 5.3.2.2.6.3 Room Temperature ShearSubject specimens to a ten-sile shear test at a room temp
23、erature of 27 6 6C (80 6 10F).6.4 Low Temperature ShearTest specimens at 54 6 3C(65 6 5F). Bring the specimens to temperature as indicatedby a thermocouple at the bond area and stabilize for 10 6 1min just prior to test. Stabilize the chamber used to test thespecimens at the test temperature for 45
24、min prior to testing.6.5 High Temperature ShearTest specimens at93 + 0, 3C (200 + 0, 5F). Bring the specimens to tem-perature as indicated by a thermocouple at the bond area andstabilize for 10 min just prior to test. Stabilize the chamberused to test the specimens at the test temperature for 45 min
25、prior to testing.6.6 Humidity ExposureTest lap shear specimens at 93 63C (200 6 5F) after 2 weeks exposure to 100 % relativehumidity and 93 6 3C (200 6 5F). Bring the specimen totemperature as indicated by a thermocouple at the bond areaand stabilize for 10 min just prior to test. Stabilize the cham
26、berused to test the specimens at temperature and humidity for 45min prior to testing. Start the test of each humidity exposuretest specimen no later than 30 min after removing it from thehumidity chamber.6.7 Salt Spray ExposureTest specimens at 27 6 6C (806 10F) after exposure to the salt spray test
27、 of MIL-STD-202Fusing a 20 % NaCl solution at 35 6 3C (95 6 5F). Stabilizethe specimens at the test temperature as indicated by athermocouple at the bond area for 10 min just prior to test.7. Inspection7.1 Qualification InspectionThe inspection requirementsspecified herein are classified as follows:
28、7.1.1 Qualification TestUnless otherwise specified by thepurchaser, adhesives that have not passed the qualificationtests, or that have previously passed the tests but havesubsequently been modified in any manner, shall be testedagainst this specification and shown to meet its requirements.7.1.1.1 I
29、nstruction SheetA dated, coded, and titled in-struction sheet that outlines instruction for use of the adhesiveon bonding metal facings to foam core and metal componentsshall be supplied by the manufacturer. These instructions shallbe forwarded with the test report when requesting qualification.In a
30、ddition, a copy of the instruction sheet shall accompanyeach shipment of the adhesive.7.1.2 Reevaluation ProcedureIn the event that two ormore test results should fall below the minimum specified forany of the qualification tests, the submitted product shall beconsidered to have failed qualification
31、 testing. In this case, thelot along with two additional lots may be retested for that test.If all of these pass, the product will be considered as beingqualified.7.2 Quality Conformance Inspection The number of testspecimens for conformance testing shall be five. The testprocedure, cure of the adhe
32、sive, and surface preparation shallbe in accordance with 6.2.7.2.1 TestsSamples of each lot of adhesive delivered oncontract of order shall be subjected to the following qualityconformance tests. Test reports, in duplicate, shall be furnishedfor all quality conformance tests specified in this specif
33、ication,and shall be signed by an authorized representative of thelaboratory making the tests. Acceptance or approval of mate-rials during the course of manufacture shall not be construed asa guarantee of acceptance of the finished product.7.2.2 Room Temperature Shear (Acceptance)The roomtemperature
34、 shear strength test shall be conducted in accor-dance with 6.3 using 6061-T6 aluminum alloy.7.2.3 High Temperature Shear (Acceptance)The hightemperature shear test shall be conducted in accordance with6.3 using 6061-T6 aluminum alloy.TABLE 1 Physical Property RequirementsTest RequirementRoom temper
35、ature, shear 2000 psi, min, 13.8 MPaLow temperature, shear 2000 psi, min, 13.8 MPaHigh temperature, shear 1500 psi, min, 10.3 MPaHumidity exposure, shear, hot 1500 psi, min, 10.3 MPaSalt spray exposure, shear, RT 2000 psi, min, 13.8 MPaE17940328. Packaging and Package Marking8.1 PackagingPackaging s
36、hall be in accordance with thesuppliers standard practices and applicable regulation Theproduct shall be clearly and legibly labeled with the followinginformation:8.1.1 Specification number,8.1.2 Date of manufacture (month and year),8.1.3 Manufacturers name and address,8.1.4 Manufacturers product de
37、signation,8.1.5 Manufacturers batch and lot designation,8.1.6 Contract number,8.1.7 Expiration date,8.1.8 Manufacturers recommended storage temperaturerange, and8.1.9 Quantity contained.9. Keywords9.1 adhesive; elevated humidity; foam and beamASTM International takes no position respecting the valid
38、ity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subje
39、ct to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquart
40、ers. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard
41、 is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).E1794033