1、Designation: F2479 12 (Reapproved 2017) An American National StandardStandard Guide forSpecification, Purchase, Installation and Maintenance ofPoured-In-Place Playground Surfacing1This standard is issued under the fixed designation F2479; the number immediately following the designation indicates th
2、e year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This guide covers information with regard to the d
3、esign,manufacture, installation, and maintenance of poured-in-placeplayground surfaces.NOTE 1This document is a guide and not intended to be used as aspecification; it should be used for educational purposes.1.2 This guide outlines the issues of compliance withexisting standards, durability, and fun
4、ctional longevity.1.3 This guide reviews issues such as edge treatment,abutting surfaces, and combinations with other surfaces de-signed for circulation or protective surfaces.1.4 This guide presents maintenance considerations andgeneral procedures that should be followed by the owner/operator.1.5 T
5、his guide outlines aging considerations such as loss ofimpact absorption, cracking, shrinkage, heaving, and how toprevent, accommodate, or rectify those issues.1.6 This guide presents warranty considerations.1.7 This guide does not imply that an injury cannot beincurred when the surface system is co
6、mpliant with thestandards referred to in this guide.1.8 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.9 This standard does not purpor
7、t to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.1.10 This international standard was developed i
8、n accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2
9、.1 ASTM Standards:2F1292 Specification for Impact Attenuation of SurfacingMaterials Within the Use Zone of Playground EquipmentF1951 Specification for Determination of Accessibility ofSurface Systems Under and Around Playground Equip-ment2.2 CSA Standard:3CSA Z614 Childrens Playspaces and Equipment3
10、. Terminology3.1 Definitions:3.1.1 aliphatic prepolymerprepolymer which does notcontain any 1,3,5-cyclohexatrien group.3.1.1.1 DiscussionGenerally highly color stable when ex-posed to UV radiation, no yellowing.3.1.2 ambient grindingprocess that takes raw rubber prod-ucts and processes it to rubber
11、crumb, chips, buffings, and soforth that is at the temperature generated by the grindingequipment or in the location of production.3.1.3 aromatic prepolymerhydrocarbons that are madefrom only hydrogen and carbon and contain a prepolymerwhich contains one or more 1,3,5-cyclohexatriene group.3.1.3.1 D
12、iscussionAromatic prepolymer are generallysusceptible to change when exposed to UV and moisture.These changes can be seen as a yellowish shading or “amber-ing” of the top surface, especially when encapsulating rubbercrumb that is grey, light blue, blue, eggshell, teal, and so forth.3.1.4 asphalt, ad
13、jacentbituminous bound material that isused as a curb or walkway and comes into contact with thepoured-in-place surface.1This guide is under the jurisdiction of ASTM Committee F08 on SportsEquipment, Playing Surfaces, and Facilities and is the direct responsibility ofSubcommittee F08.63 on Playgroun
14、d Surfacing Systems.Current edition approved April 1, 2017. Published April 2017. Originallyapproved in 2007. Last previous edition approved in 2012 as F2479 12. DOI:10.1520/F2479-12R17.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceas
15、tm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from Canadian Standards Association (CSA), 5060 Spectrum Way,Mississauga, ON L4W 5N6, Canada, http:/www.csa.ca.Copyright ASTM International, 100 Barr Harbor Drive,
16、PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued
17、 by the World Trade Organization Technical Barriers to Trade (TBT) Committee.13.1.4.1 DiscussionThe materials and compaction shallconform to local engineering practices and have a mechanicalcompaction of no less than 98 % standard proctor density. Theedge of the asphalt at the junction with the pour
18、ed-in-placesurface shall be vertical to 30 from horizontal. Considerationshould be given to the use of an appropriate primer asrecommended by the manufacturer to ensure adhesion of thepoured-in-place surface to the asphalt.3.1.5 asphalt, basehard, bituminous bound surface that isunder the poured-in-
19、place surface.3.1.5.1 DiscussionNew asphalt should cure at least 14days, have no residual surface oils, and be pressure washed orhave at least two thorough rainfalls prior to receiving poured-in-place surface. When the surface is flooded with as much as0.2 in. (5.1 mm) of water, there should be no e
20、vidence(rainbow effect) of oils on the surface of the water. A properlyprepared asphalt base will be able to effectively remove anywater which penetrates the poured-in-place surface. This maybe accomplished by sloping the asphalt, installing drainage, orusing porous asphalt.3.1.6 concrete, baseconcr
21、ete surface that is under thepoured-in-place surface.3.1.6.1 DiscussionThe concrete base should be 4 in. (100mm) minimum thickness. All new concrete slabs should curefor a minimum of seven days prior to receiving poured-in-placesurface. Concrete base should have a medium broom finish. Aproperly prep
22、ared concrete base will be able to effectivelyremove any water which penetrates the poured-in-place sur-face. This may be accomplished by sloping the concrete,installing drainage, or using a porous concrete.3.1.7 concrete, adjacentconcrete material that is used as acurb or walkway and comes into con
23、tact with the poured-in-place surface3.1.7.1 DiscussionThe materials and compaction shallconform to local engineering practices and have a moisturecontent less than 5 % at the time the poured-in-place surface isinstalled. The edge of the concrete at the junction with thepoured-in-place surface shall
24、 be vertical. Consideration shouldbe given to the use of an appropriate primer as recommendedby the manufacturer to ensure adhesion of the poured-in-placesurface to the concrete. Other strategies to avoid sinking of thefinal poured-in-place surface would be to provide a “key” or“step” in the vertica
25、l face of the concrete to support thepoured-in-place surface.3.1.8 cryogenic grindingprocess that takes a raw rubberproduct and processes it to rubber crumb, chips, and so forth,a process that freezes the raw product and the frozen product isground to the specification.3.1.9 gravel, base mixture of
26、crushed stone, sand, or boththat is compacted to not less than 95 % standard proctordensity.3.1.9.1 DiscussionA geotextile may be required betweenthe granular base and poured-in-place surface to ensure that theparticles of the granular base do not contaminate the poured-in-place surface. If fine par
27、ticles from the base migrate into thepoured-in-place system the void content of the system isreduced and the ability to attenuate force is reduced.3.1.10 drainage, sub-surfaceprovision of a method ofremoving water below the poured-in-place surface.3.1.10.1 DiscussionThis can be achieved by sloping t
28、hesub-base material where it has a high clay content, usingdrainage channels or pipes, installing a granular drainage layerfor percolation.3.1.11 drainage, surfacesloping of the surface to allowwater to travel across the surface to a drain.3.1.11.1 DiscussionThe porosity of the poured-in-placesurfac
29、e allows water to pass through more quickly than acrossit unless it is fully saturated.3.1.12 EPDM rubber productproduct comprised of or-ganic and inorganic materials with a minimum of 20 % and amaximum of 26 % of ethylene propylene-diene-saturatedpolymethylene main chain along with other organic an
30、dinorganic components. The rubber can be either peroxide orsulphur cured.3.1.13 functional longevityability of the poured in placesurface to continue to comply with relevant ASTM standardsand not require replacement.3.1.13.1 DiscussionThere are circumstances where thepoured-in-place surface is physi
31、cally in place however becauseof failures with regard to the stated performance criteria, thesurface needs to be replaced. The functional longevity can bestated in years or by comparison to the functional life of theplay structure as stated in writing by the play structuremanufacturer.3.1.14 gravel,
32、 drainage layeropen course of granularmaterial that is installed as a layer or in channels to promoteremoval of water from a location.3.1.14.1 DiscussionThe layer should have a slope thatpromotes the removal of water.3.1.15 humidity/moisture effectschanges in the poured-in-place system caused by flu
33、ctuations in absolute humidity orexposure to moisture during the storage of materials,installation, and cure.3.1.15.1 DiscussionPolyurethane binders are reactive tomoisture in varying degrees, depending upon formulation. Allone-component polyurethane binders will require some degreeof moisture to af
34、fect a cure of the product. Dramatic changes inmoisture or absolute humidity can cause variable finishes in thesurface if they are not accounted for. During installation, somepoured-in-place surfaces require dry conditions, while otherscan be installed during a light rain and others can have waterap
35、plied directly to the surface. Exposure to water may causethe binder to foam and which may reduce the effectiveness ofthe bond. Moisture in the rubber that is mixed with the bindermay also have an effect on the outcome of the project if notaccounted for. One strategy to eliminate this problem is to
36、havethe rubber stored in a dry place and if this is not possible, therubber should be covered with tarps or other methods em-ployed to prevent moisture from entering the materials.3.1.16 lacquerspolyurethane-based product that containssolvents applied as a top coat in a spray or roller application.3
37、.1.16.1 DiscussionThis product is used to provide colorthrough the addition of a pigment, protection, or both fromexposure to ultraviolet light.F2479 12 (2017)23.1.17 latex binderspolymer binder that is water-basedthat has thermoplastic properties.3.1.17.1 DiscussionGenerally, the flexibility perfor
38、manceis within a narrow range of temperature. Latex has also beenassociated with allergic reactions once it has cured. There is aconcern for children with exposed skin coming into contactwith this binder, as well persons with disabilities who have apropensity to allergic reactions to latex.3.1.18 po
39、lymer binderssynthetic binders used in themanufacture of the poured-in-place surface that coat theindividual rubber chips, crumb, or buffings.3.1.18.1 DiscussionThese binders are to provide flexibil-ity to allow the rubber particles to move in relation to oneanother and have the strength to stop the
40、 bond from breakingat maximum elongation. These binders are man-made frompetrochemicals and some of these demonstrate flexibility at arange of temperatures that children are expecting to use theplayground and specifically to allow compliance with Specifi-cation F1292. Polymer binders with a glass tr
41、ansition tempera-ture above 22F (30C) and with high sensitivity to damageby submersion in water are to be avoided.3.1.19 polyurethanepolymer binder that demonstratesflexibility and strength over a wide range of temperatures.3.1.19.1 DiscussionPolyurethane is manufactured in bothone-component (moistu
42、re cured) and two-component (mixingpart A and part B in a specified ratio). Binders used inpoured-in-place surfaces are almost always of the one-component type. Certain polyurethane binders can be damagedthrough exposure to ultraviolet light and immersion in water.UV-resistant polyurethane lacquers
43、may be applied to thesurface following installation of the poured-in-place surface.These lacquers are typically two-component. Once cured,polyurethane produces no known allergic reactions.3.1.20 recycled black EPDM rubbercrumb manufacturedthrough ambient or cryogenic grinding or crushing of postindu
44、strial scrap, containing a mixture of types of rubberincluding EPDM rubber product and varying in size. Thisrubber must have a minimum of 4 % actual EPDM content.3.1.20.1 DiscussionThe actual percentage of EPDM con-tent will be significantly less than new EPDM rubber productdue to the inclusion of o
45、ther industrial scrap rubber that issourced in the recycling process.3.1.21 recycled post consumer or industrial rubber rubbercrumb that is the result of granulating in an ambient orcryogenic process from a variety of scrap rubber produced asa part of an industrial process or at the end of an indust
46、rial orconsumer good made of rubber.3.1.21.1 DiscussionThis is manufactured into rubbercrumb as the feedstock and is often of limited dimension. Thevariety of rubber can be very large in that this can include anywaste rubber from a manufacturing process or post consumeruse.3.1.22 recycled tire rubbe
47、rrubber crumb, chips, or buff-ings made from post manufacturing of tires or post consumertires.3.1.22.1 DiscussionThis rubber can vary in its content asa result of the type of tire (automobile, truck, off road, and soforth) that is ground.3.1.23 release agentsmaterials that prevent the bonding ofthe
48、 polyurethane to other surfaces.3.1.23.1 DiscussionThese can be waxes, silicone, or pe-troleum jelly.3.1.24 rubber buffngsstrands of rubber that are productshavings of rubber feedstock, typically tires, ranging in sizefrom 0.079 to 0.87 in. (2 to 20 mm) in length and 0.039 to0.157 in. (1 to 4 mm) in
49、 width.3.1.25 rubber chipsparticles of rubber that have beenproduced by ambient or cryogenic grinding of rubber feedstockto a size of 0.197 to 0.59 in. (5 to 15 mm).3.1.26 rubber crumbparticles of rubber that have beenproduced by ambient or cryogenic grinding of rubber feedstockto a size of between 0.02 and 0.197 in. (0. 5 and 5 mm).3.1.26.1 DiscussionRubber crumb shall contain less than2 % rubber dust, fine rubber passing a 0.85 mm screen, as thiscan consume binder and affect the performance and longevityof the surface. The su