1、BS EN1301-2:2008ICS 77.150.10NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBRITISH STANDARDAluminium andaluminium alloys Drawn wirePart 2: Mechanical propertiesThis British Standardwas published under theauthority of the StandardsPolicy and StrategyCommittee on 31 October2008
2、 BSI 2008ISBN 978 0 580 56394 2Amendments/corrigenda issued since publicationDate CommentsBS EN 1301-2:2008National forewordThis British Standard is the UK implementation of EN 1301-2:2008. Itsupersedes BS EN 1301-2:1997 which is withdrawn.The UK participation in its preparation was entrusted to Tec
3、hnicalCommittee NFE/35, Light metals and their alloys.A list of organizations represented on this committee can be obtained onrequest to its secretary.This publication does not purport to include all the necessary provisionsof a contract. Users are responsible for its correct application.Compliance
4、with a British Standard cannot confer immunityfrom legal obligations.BS EN 1301-2:2008EUROPEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN 1301-2September 2008ICS 77.150.10 Supersedes EN 1301-2:1997 English VersionAluminium and aluminium alloys - Drawn wire - Part 2:Mechanical propertiesAluminium et al
5、liages daluminium - Fil tir - Partie 2:Caractristiques mcaniquesAluminium und Aluminiumlegierungen - Gezogene Drhte -Teil 2: Mechanische EigenschaftenThis European Standard was approved by CEN on 16 August 2008.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate
6、 the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may be obtained on application to the CEN Management Centre or to any CEN member.This European Standard exists
7、in three official versions (English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as theofficial versions.CEN members are the national standards bodies
8、of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN
9、COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMITEE FR NORMUNGManagement Centre: rue de Stassart, 36 B-1050 Brussels 2008 CEN All rights of exploitation in any form and by any means reservedworldwide for CEN national Members.Ref. No. EN 1301-2:2008: EBS EN 1301-2:2008EN 13
10、01-2:2008 (E) 2 Contents Page Foreword3 1 Scope 4 2 Normative references 4 3 Tensile test .4 Annex A (normative) Rules for rounding11 Bibliography 12 BS EN 1301-2:2008EN 1301-2:2008 (E) 3 Foreword This document (EN 1301-2:2008) has been prepared by Technical Committee CEN/TC 132 “Aluminium and alumi
11、nium alloys”, the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by March 2009, and conflicting national standards shall be withdrawn at the latest by March 20
12、09. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. CEN/TC 132 affirms it is its policy that in the case when a patentee refuses to gr
13、ant licenses on standardised standard products under reasonable and not discriminatory conditions, then this product shall be removed from the corresponding standard. This document supersedes EN 1301-2:1997. Within its programme of work, Technical Committee CEN/TC 132 entrusted CEN/TC 132/WG 4 “Wire
14、s and drawing stock“ to revise EN 1301-2:1997. Besides editorial adjustments in the text and update of normative references the following changes have been made: Foreword amended; Clause 2: EN 573-3 deleted and included in Bibliography; Tables 1 to 6: Footnotes modified; Table 2: Tempers H13 and H18
15、 added for alloy EN AW-2011 and temper H18 added for alloys EN AW-2014A, EN AW-2017A, EN AW-2117 and EN AW-2024; Table 5: Alloy EN AW-6056 added and temper H18 added for alloys EN AW-6061 and EN AW-6082; Table 6: Temper H18 added. EN 1301 comprises the following parts under the general title: “Alumi
16、nium and aluminium alloys Drawn wire“: Part 1: Technical conditions for inspection and delivery Part 2: Mechanical properties Part 3: Tolerances on dimensions According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement thi
17、s European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the
18、United Kingdom. BS EN 1301-2:2008EN 1301-2:2008 (E) 4 1 Scope This document specifies the mechanical properties of aluminium and aluminium alloy drawn wires for general engineering applications (except aeronautical rivets). It applies to drawn wires, except for electrical or welding purposes. It doe
19、s not apply to drawing stock. The designation of aluminium and aluminium alloys, their chemical composition and the temper designations used in this standard are in accordance with EN 573- 3 and EN 515 respectively. 2 Normative references The following referenced documents are indispensable for the
20、application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 515:1993, Aluminium and aluminium alloys Wrought products Temper designations EN 1301-1, Aluminium and alum
21、inium alloys Drawn wire Part 1: Technical conditions for inspection and delivery EN 10002-1, Metallic materials Tensile testing Part 1: Method of test at ambient temperature 3 Tensile test The conditions for the sampling shall be in accordance with EN 1301-1. The testing conditions specified in EN 1
22、0002-1 shall apply together with the following additional conditions: full section test pieces shall be used; elongation shall be measured on a reference length of 100 mm. Tensile strength shall conform to Tables 1 to 6. NOTE Typical values for proof stress and elongation,are given for information o
23、nly. Tensile strength values shall be rounded in accordance with Annex A. For rivet wire in non heat treatable alloys delivered in H13 temper the mechanical properties shall be determined in the temper of delivery. For rivet wire in heat treatable alloys delivered in H13 temper, the mechanical prope
24、rties shall be determined: a) in the delivered temper H13; b) and also in tempers: 1) T4 for EN AW-2017A, EN AW-2117 and EN AW-2024 alloys; 2) T6 for EN AW-2014A, EN AW-6061, EN AW-6082 and EN AW-7075 alloys. BS EN 1301-2:2008EN 1301-2:2008 (E) 5 Testing may also be made in T42 temper or T62 temper
25、(EN 515:1993, 7.3.2), instead of T4 or T6 respectively. In this case the mechanical properties limits are those given for the corresponding T4 and T6 tempers. Table 1 Series 1 000 (Al) Temper Diameter Tensile strength Proof stress Elongationad up to and including RmRp0,2 aA100 mmmm MPa MPa % Materia
26、l designation min. max. typical typical O 20 - 70 - 25 EN AW-1098 AI 99,98 H14 18 85 - 80 3 H18 10 115 110 2 O 20 - 80 - 35 EN AW-1080A AI 99,8 (A) H14 18 90 - 85 5 H18 10 120 115 3 O 20 - 85 - 35 EN AW-1070A AI 99,7 H14 18 95 - 90 5 H18 10 125 120 3 O 20 - 95 - 35 EN AW-1050A AI 99,5 H14 18 100 - 9
27、5 5 H16 15 120 115 3 18 10 140 - 135 aThe typical proof stress and elongation values are for information only and are influenced by the wire diameter and the method of drawing. BS EN 1301-2:2008EN 1301-2:2008 (E) 6 Table 2 Series 2 000 (Al Cu) Temper Diameter Tensile strength Proof stress Elongation
28、ad up to and including RmRp0,2 aA100 mmmm MPa MPa % Material designation min. max. typical typical EN AW-2011 AI Cu6BiPb T3 18 310 - 295 6 T8 370 310 4 H13 18 155 225 - - 18 10 240 - H13 b18 210 280 190 5 EN AW-2014A AI Cu4SiMg (A) T4 18 380 - 255 18 T6 440 415 9 H18 10 295 - - - EN AW-2017A AI Cu4M
29、gSi (A) H13 b18 210 300 190 5 T4 18 380 - 255 18 H18 10 315 - - EN AW-2117 AI Cu2,5Mg H13 b18 170 240 110 5 T4 18 260 - 160 20 H18 10 260 - - EN AW-2024 AI Cu4Mg1 H13 b18 230 300 200 5 T4 18 420 - 315 18 H18 10 320 - - aThe typical proof stress and elongation values are for information only and are
30、influenced by the wire diameter and the method of drawing. bMechanical properties shall also be tested in T4 temper (alloys EN AW-2017A, EN AW-2117 and EN AW-2024) or T6 temper (alloy EN AW-2014A). Testing may also be made in T42 temper or T62 temper (EN 515:1993, 7.3.2), instead of T4 or T6 respect
31、ively. In this case the mechanical properties limits are those given for the corresponding T4 and T6 tempers. BS EN 1301-2:2008EN 1301-2:2008 (E) 7 Table 3 Series 3 000 (Al Mn) Temper Diameter Tensile strength Proof stress Elongationad up to and including RmRp0,2 aA100 mmmm MPa MPa % Material design
32、ation min. max. typical typical O 20 - 130 60 35 EN AW-3003 AI Mn1Cu H14 18 135 180 120 5 H18 10 180 - 175 3 O 20 - 130 60 35 EN AW-3103 AI Mn1) H14 18 135 180 120 5 H18 10 170 - 165 3 aThe typical proof stress and elongation values are for information only and are influenced by the wire diameter an
33、d the method of drawing. BS EN 1301-2:2008EN 1301-2:2008 (E) 8 Table 4 Series 5 000 (Al Mg) Temper Diameter Tensile strength Proof stress Elongationad up to and including RmRp0,2 aA100 mmmm MPa MPa % Material designation min. max. typical typical O 20 - 195 85 15 EN AW-5051A AI Mg2 (B) H12 18 170 22
34、0 155 6 H14 195 245 200 4 18 10 245 - 3 O 20 - 215 95 15 EN AW-5251 AI Mg2Mn0,3 H14 18 215 265 220 4 H18 10 265 - 270 3 O 20 - 225 100 15 14 18 225 275 225 4 EN AW-5052 AI Mg2,5 H18 10 275 - 275 3 H32 18 190 240 145 11 34 15 215 265 195 8 38 10 260 - 245 5 O 20 - 275 125 16 H14 18 280 330 270 3 18 1
35、0 330 - 320 2 EN AW-5154A AI Mg3,5 (A) H32 18 235 285 170 11 H34 15 265 315 230 8 36 10 290 340 250 6 38 310 - 280 4 O 20 - 250 110 16 H12 18 230 280 200 6 14 255 305 250 3 EN AW-5754 AI Mg3 H18 10 305 - 300 2 H32 18 220 270 160 11 34 15 245 295 210 8 H38 10 290 - 260 4 O 20 - 330 150 17 H12 18 295
36、355 255 6 14 325 385 315 3 EN AW-5019 AI Mg5 H18 18 370 - 360 2 H32 280 340 205 11 34 15 310 370 265 8 38 10 360 - 320 4 aThe typical proof stress and elongation values are for information only and are strongly influenced by the wire diameter and the method of drawing. BS EN 1301-2:2008EN 1301-2:200
37、8 (E) 9 Table 5 Series 6 000 (Al MgSi) Temper Diameterd Tensile strength RmProof stress Rp0,2 aElongationaA100 mmmm MPa MPa %Material designation min. max. typical typical H13b 18 160 240 140 4 H18 10 240 - 210 2 T39 c 6 400 - - - EN AW-6056 AI Si1MgCuMn T39 c 6 360 - - - T4 20 300 380 - 13 T6 20 40
38、0 - 360 10 T89 c 6 420 - - - T39 c 6 220 - - - EN AW-6060 AI MgSi T39 c 6 270 - - - T4 20 140 210 90 13 T6 20 210 - 160 10 T89 c 6 260 - - - H13b 18 150 210 120 4 H18 10 210 - - - EN AW-6061 AI Mg1 SiCu T39 c 6 310 - - - T39 c 6 260 - - - T4 20 205 285 135 13 T6 20 290 - 260 10 T89 c 6 300 - - - T39
39、 c 6 230 - - - T39 c 6 280 - - - EN AW-6063 AI Mg0,7Si T4 20 150 - 100 13 T6 20 220 - 190 10 T89 c 6 270 - - - H13b 18 165 225 130 4 H18 10 220 - 200 2 T39 c 6 310 - - - EN AW-6082 AI SiMgMn T39 c 6 360 - - - T4 20 205 285 135 13 T6 20 300 - 270 10 T89 c 6 340 - - - aThe typical proof stress and elo
40、ngation values are for information only and are influenced by the wire diameter and the method of drawing. bMechanical properties shall also be tested in T6 temper. Testing may also be made in T62 temper (EN 515:1993, 7.3.2), instead of T6. In this case the mechanical properties limits are those giv
41、en for the corresponding T6 tempers. cFor these tempers the mechanical properties are very dependent on the amount of cold work and, for T89 temper, on the ageing conditions. It is recommended that these characteristics should be agreed between supplier and purchaser. Consequently, typical values of
42、 Rp0,2and elongation are not given. BS EN 1301-2:2008EN 1301-2:2008 (E) 10 Table 6 Series 7 000 (Al Zn) Temper Diameter Tensile strength Proof stress Elongation ad up to and including RmRp0,2 aA100 mmmm MPa MPa % Material designation min. max. typical typical O 20 - 275 110 13 EN AW-7075 AI Zn5,5MgC
43、u H13 b18 230 310 230 2,5 H18 10 285 - 260 2 T6 20 510 485 10 aThe typical proof stress and elongation values are for information only and are influenced by the wire diameter and the method of drawing. bMechanical properties shall also be tested in T6 temper. Testing may also be made in T62 temper (
44、EN 515:1993, 7.3.2), instead of T6. In this case the mechanical properties limits are those given for the corresponding T6 tempers. BS EN 1301-2:2008EN 1301-2:2008 (E) 11 Annex A (normative) Rules for rounding In recording test results, the number representing the results of a test to determine a gi
45、ven property shall be expressed to the same number of decimal places as the corresponding number in this standard, except for elongation values which shall be recorded with one more decimal place. The following rounding rules shall be used for determination of compliance with this standard: a) when
46、the figure immediately after the last figure to be retained is less than 5, the last figure to be retained remains unchanged; b) when the figure immediately after the last figure to be retained is greater than 5, or equal to 5 and followed by at least one figure other than zero, the last figure to b
47、e retained is increased by one; c) when the figure immediately after the last figure to be retained is equal to 5 and followed by zeros only, the last figure to be retained remains unchanged if even and is increased by one if odd. BS EN 1301-2:2008EN 1301-2:2008 (E) 12 Bibliography 1 EN 573-3, Alumi
48、nium and aluminium alloys Chemical composition and forms of wrought products Part 3 : Chemical composition and form of products BS EN 1301-2:2008This page has been intentionally left blank BS EN1301-2:2008BSI GroupHeadquarters 389Chiswick High Road,London, W4 4AL, UKTel +44 (0)20 8996 9001Fax +44 (0)20 8996 - British Standards InstitutionBSI is the independent national body responsible for