1、AMSC N/A FSC 5340 MS35827E 30 JUNE 2010 SUPERSEDING MS35827D 6 JANUARY 1989 DETAIL SPECIFICATION SHEET HINGE, CONTINUOUS (PIANO) .060 THICKNESS, .250 PIN DIA. This specification sheet is approved for use by all Departments and Agencies of the Department of Defense. The requirements for acquiring the
2、 product described herein shall consist of this specification sheet and procurement specification MIL-H-9850. BAIMPRESS PART NUMBER AT A MAXIMUM OF 3 INCH INTERVALSDP.060OPENING.020 MAX275 MINGFSTOCK LENGTH - 120 (SEE NOTE)END LOOPS SHALL BE A MINIMUM OF 1/2FIGURE I. Hinge. TABLE I. Dash Numbers and
3、 Dimensions. DASH NO. WIDTH STOCK LENGTH L .03 KNUCKLE LENGTH 1/ D PITCH 2/ P KNUCKLE F PIN G A REF B .031 1 1.500 .750 120 SEE NOTE 2 .998 2.000 .253 +.007 -.001 .250 +.000 -.002 2 2.000 1.000 +.000 +.015 3 2.500 1.250 -.015 -.003 4 3.000 1.500 5 3.000 1.500 1.998 4.000 6 3.500 1.750 +.000 +.015 7
4、4.000 2.000 -.015 -.003 8 5.000 2.500 1/ See requirement 3. 2/ See requirement 4. INCH-POUNDInactive for new design after 22 January 1976.Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MS35827E 2Requirements: 1. Material - A. Aluminum-leaf-temper, H
5、24 or H34 Alloy 5052 (UNS A95052) in accordance with SAE-AMS-QQ-A-250/8. Aluminum-pin-temper, H34 Alloy 5052, (UNS A95052) in accordance with ASTM B211. B. Brass-leaf-alloy 268 (UNS C26800) temper H02, in accordance with ASTM B36/B36M Copper-pin-alloy 260 (UNS C26000) temper H02, in accordance with
6、ASTM B134/B134M. C. Corrosion resistant steel-leaf, temper annealed composition 301 (UNS S30100) in accordance with ASTM A666, 302 (UNS S30200) or 304 (UNS S30400) in accordance with ASTM A240/A240M. Corrosion resistant steel-pin composition 302 (UNS S30200), 304 (UNS 30400), 305 (UNS S30500) and 31
7、6 (UNS S31600) in accordance with ASTM A313/A313M. D. Carbon steel-leaf-cold-rolled, temper no. 4 in accordance with QQ-S-698. Carbon steel-pin-composition 1010 (UNS G10100), 1020 (UNS G10200) in accordance with ASTM A853. E. Carbon-steel-leaf-cold-rolled temper no. 4 in accordance with QQ-S-698. Co
8、pper-pin-alloy 260 (UNS C26000) temper H02 in accordance with ASTM B134/B134M. 2. Finish - Material A, B, C and D shall be plain (uncoated). When specified, material D shall be zinc plated in accordance with ASTM B633, Type II, Fe/Zn 13 or cadmium plated in accordance with SAE-AMS-QQ-P-416,type II,
9、Class 1. Material E shall be cadmium plated in accordance with SAE-AMS-QQ-P-416, Type II, Class 1. 3. Knuckles - End knuckles shall be a minimum of 1/2 of knuckle. 4. Pitch - Cumulative tolerance on pitch is .015 inches in any 36 inch segment. 5. Part number - The MS part number consists of the MS n
10、umber plus the dash number followed by the applicable code for material from requirement 1. Example: MS35827 - 6 B Material code Dash number Basic MS number When protective finish is required for material D, add F to the part number. Provided by IHSNot for ResaleNo reproduction or networking permitt
11、ed without license from IHS-,-,-MS35827E 3Notes: 1. All dimensions are in inches unless otherwise specified. 2. Hinges shall be stocked and issued in lengths of 120.00 inches. Application may be of any length within the above length. 3. In the event of a conflict between the text of this standard an
12、d the references cited herein, the text of this standard shall take precedence. 4. Changes from previous issue. Marginal notations are not used in this revision to identify changes with respect to the previous issue due to the extent of the changes. Custodians: Preparing Activity: Army - AT DLA -IS
13、Navy - AS Air force - 99 (Project 5340-2010-019) Review activity: Army - AV Navy - MC Air force - 71 Note: the activities listed above were interested in this document as of the date of this document. Since organizations and responsibilities can change, you should verify the currency of the information above using the assist online database at https:/assist.daps.dla.mil. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-