1、BSI Standards PublicationBS EN ISO 3167:2014Incorporating corrigendum October 2014BS EN ISO 3167:2014Plastics Multipurpose testspecimens (ISO 3167:2014)BS EN ISO 3167:2014 BRITISH STANDARDNational forewordThis British Standard is the UK implementation of EN ISO 3167:2014. It supersedes BS EN ISO 316
2、7:2003 which is withdrawn.The UK participation in its preparation was entrusted to Technical Committee PRI/21, Testing of plastics.A list of organizations represented on this committee can be obtained on request to its secretary.This publication does not purport to include all the necessary provisio
3、ns of a contract. Users are responsible for its correct application. The British Standards Institution 2014. Published by BSI Standards Limited 2014ISBN 978 0 580 87951 7ICS 83.080.01Compliance with a British Standard cannot confer immunity from legal obligations.This British Standard was published
4、under the authority of the Standards Policy and Strategy Committee on 31 August 2014.Amendments/corrigenda issued since publicationDate Text affected31 October 2014 Implementation of CEN Correction Notice 27 August 2014: Supersession information updatedEUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NO
5、RM EN ISO 3167 August 2014 ICS 83.080.01 Supersedes EN ISO 3167:2003English Version Plastics - Multipurpose test specimens (ISO 3167:2014) Plastiques - prouvettes usages multiples (ISO 3167:2014) Kunststoffe - Vielzweckprobekrper (ISO 3167:2014) This European Standard was approved by CEN on 23 July
6、2014. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtaine
7、d on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-C
8、ENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, I
9、taly, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: A
10、venue Marnix 17, B-1000 Brussels 2014 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 3167:2014 EEN ISO 3167:2014 (E) 3 Foreword This document (EN ISO 3167:2014) has been prepared by Technical Committee ISO/TC 61 “Plastics” in
11、collaboration with Technical Committee CEN/TC 249 “Plastics” the secretariat of which is held by NBN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by February 2015, and conflicting national standa
12、rds shall be withdrawn at the latest by February 2015. This document supersedes EN ISO 3167:2003. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such pat
13、ent rights. According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia,
14、 France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. Endorsement notice The text of ISO 3167:2014 has been approved by CEN as EN
15、 ISO 3167:2014 without any modification. BS EN ISO 3167:2014EN ISO 3167:2014 (E)BS EN ISO 3167:2014ISO 3167:2014(E) ISO 2014 All rights reserved iiiContents PageForeword iv1 Scope . 12 Normative references 13 Dimensions of test specimens 14 Preparation of test specimen 24.1 General . 24.2 Injection
16、moulding of multipurpose test specimens 34.3 Compression moulding of multipurpose test specimens . 34.4 Machining of multipurpose test specimens . 35 Report on preparation of test specimens . 3Annex A (informative) Recommended applications for multipurpose test specimens or parts thereof . 5Annex B
17、(informative) Consequences of changes in geometry . 6Bibliography 8BS EN ISO 3167:2014ISO 3167:2014(E)ForewordISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally
18、 carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the w
19、ork. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.The procedures used to develop this document and those intended for its further maintenance are described in the ISO/IEC Directives, Part 1. In particular the dif
20、ferent approval criteria needed for the different types of ISO documents should be noted. This document was drafted in accordance with the editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).Attention is drawn to the possibility that some of the elements of this document m
21、ay be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of any patent rights identified during the development of the document will be in the Introduction and/or on the ISO list of patent declarations received (see www.iso.org/pate
22、nts).Any trade name used in this document is information given for the convenience of users and does not constitute an endorsement.For an explanation on the meaning of ISO specific terms and expressions related to conformity assessment, as well as information about ISOs adherence to the WTO principl
23、es in the Technical Barriers to Trade (TBT) see the following URL: Foreword - Supplementary informationThe committee responsible for this document is ISO/TC 61, Plastics, Subcommittee SC 2, mechanical properties.This fifth edition results from the reinstatement of the previous edition (ISO 3167:2002
24、) which was withdrawn in 2013.ISO 3167 is intended to be gradually replaced by ISO 20753 which specifies the designations and dimensions of test specimens used for the acquisition of comparable data, and also other frequently used specimens, in one document for ease of reference.iv ISO 2014 All righ
25、ts reservedBS EN ISO 3167:2014INTERNATIONAL STANDARD ISO 3167:2014(E)Plastics Multipurpose test specimens1 ScopeThis International Standard specifies requirements relating to multipurpose test specimens for plastic moulding materials intended for processing by injection or direct compression mouldin
26、g.Specimens of types A and B are tensile test specimens from which, with simple machining, specimens for a variety of other tests can be taken (see Annex A). Because they have such wide utility, these tensile specimens are referred to in this International Standard as multipurpose test specimens.The
27、 principal advantage of a multipurpose test specimen is that it allows all the test methods mentioned in Annex A to be carried out on the basis of comparable mouldings. Consequently, the properties measured are coherent as all are measured with specimens in the same state. In other words, it can be
28、expected that test results for a given set of specimens will not vary appreciably due to unintentionally different moulding conditions. On the other hand, if desired, the influence of moulding conditions and/or different states of the specimens can be assessed without difficulty for all of the prope
29、rties measured.For quality-control purposes, the multipurpose test specimen can serve as a convenient source of further specimens not readily available. Furthermore, the fact that only one mould is required may be advantageous.The use of multipurpose test specimens is to be agreed upon by the intere
30、sted parties, because there may be significant differences between properties of the multipurpose test specimens and those specified in the relevant test methods.2 Normative referencesThe following documents, in whole or in part, are normatively referenced in this document and are indispensable for
31、its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.ISO 293, Plastics Compression moulding of test specimens of thermoplastic materialsISO 294-1, Plastics Injection moulding of
32、 test specimens of thermoplastic materials Part 1: General principles, and moulding of multipurpose and bar test specimensISO 295, Plastics Compression moulding of test specimens of thermosetting materialsISO 2818, Plastics Preparation of test specimens by machiningISO 10724-1, Plastics Injection mo
33、ulding of test specimens of thermosetting powder moulding compounds (PMCs) Part 1: General principles and moulding of multipurpose test specimens3 Dimensions of test specimensFor the purposes of this International Standard, the preferred multipurpose test specimen is the type A tensile specimen show
34、n in Figure 1. This can be made suitable for a variety of other tests by simple cutting, because the length l1of its narrow parallel-sided portion is 80 mm 2 mm. ISO 2014 All rights reserved 1BS EN ISO 3167:2014ISO 3167:2014(E)Dimensions in millimetresSpecimen type A Bl3Overall lengtha 150Recommende
35、d valueb170 150l1Length of narrow parallel-sided portion 80 2 60,0 0,5r Radius20 to 25Recommended valueb24 1 60cRecommended valueb60,0 0,5l2Distance between broad parallel-sided portionsd104 to 113106 to 120 Recommended rangeb106 to 110b2Width at ends 20,0 0,2b1Width of narrow portion 10 0,2h Thickn
36、ess 4,0 0,2aThe recommended overall length of 170 mm for type A is consistent with ISO 294-1 and ISO 10724-1. For some materials, the length of the tabs may need to be extended (e.g. to give an overall length of 200 mm) to prevent breakage or slippage in the jaws of the test machine.bThe recommended
37、 values and ranges may become mandatory on occasion of the next revision of the standard. The lower tolerances on the radius reduce the ranges of the stress concentrations that are found at the transitions between the narrow parallel-sided and the rounded portions. Together with the smaller toleranc
38、e on the distance between the broad parallel-sided portions for type B, a common value of the initial distance between jaws can be used for tensile testing (see ISO 527-2).crll bbbb=()+()()212212214dResulting from l1, r, b1and b2, but within the indicated tolerance.Figure 1 Type A and B multipurpose
39、 test specimens4 Preparation of test specimen4.1 GeneralTest specimens shall be prepared in accordance with the relevant material specification. When none exists, specimens shall be either directly compression or injection moulded from the material in accordance with ISO 293, ISO 294-1, ISO 295 or I
40、SO 10724-1, as appropriate, or machined in accordance with ISO 2818 from plates that have been compression or injection moulded from the compound.Strict control of all conditions of the specimen preparation is essential to ensure that all test specimens in a set are actually in the same state.2 ISO
41、2014 All rights reservedBS EN ISO 3167:2014ISO 3167:2014(E)All surfaces of the test specimens shall be free from visible flaws, scratches or other imperfections. With moulded specimens all flash, if present, shall be removed, taking care not to damage the moulded surface.The broad sides of each spec
42、imen shall be suitably marked (see the note), for injection-moulded specimens to distinguish between the sides formed by the cavity plate and the fixed plate of the mould (see ISO 294-1 or ISO 10724-1), for compression-moulded and machined specimens to identify any asymmetry resulting from the under
43、lying moulding process.NOTE Asymmetry with respect to thickness can influence the flexural properties, including the temperature of deflection under load (see Annex A).For injection-moulded specimens, the sides can be identified by the impressions of the ejection pins and by the draft angle. Compres
44、sion-moulded and machined specimens shall be marked at their shoulders. ISO bars taken from the central part of multipurpose test specimens shall be marked outside their central 40 mm section, which is loaded by flexural testing.4.2 Injection moulding of multipurpose test specimensType A test specim
45、ens shall be injection moulded as specified in ISO 294-1 or ISO 10724-1, as appropriate, and under conditions defined in the relevant International Standard for the material under examination.4.3 Compression moulding of multipurpose test specimensType B test specimens shall be compression moulded di
46、rectly to their final dimensions as specified in ISO 293 or ISO 295, as appropriate, and under conditions defined in the relevant International Standard for the material under examination.4.4 Machining of multipurpose test specimens4.4.1 Machining of test specimens shall be performed either as speci
47、fied in ISO 2818 or as agreed upon by the interested parties.4.4.2 Test specimens having a width of 10 mm shall be cut symmetrically from the central parallel-sided portion of the multipurpose test specimen.The surface of the central parallel-sided portion of the test specimen shall remain as moulde
48、d: The width of the machined portions of the specimen shall be not less than that of the central parallel-sided portion, but may exceed the width of the latter by not more than 0,2 mm. During the machining operation, care shall be taken to avoid any damage to the moulded surfaces of the central port
49、ion.For test specimens longer than 80 mm, the broad ends of the type A multipurpose test specimen (or type B for test specimens longer than 60 mm) shall be machined to the width of the central parallel-sided portion.4.4.3 Type B multipurpose test specimens shall be machined from suitably processed compression-moulded plates (see 4.3).5 Report on preparation of test specimensThe report shall contain the following information:a) a reference to this International Standard;b) an indication of the specimen type (A or B); ISO