1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 01 06 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, HOWELL PATTERN, WARP KNIT WSS-M1H1019-A 1. SCOPE The material defined by this specification is a HOWELL PATTER
2、N, 3 bars, 56 Gauge, Single Needle bar, body cloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for 2008 U377 MERCURY MARINER seat bolster. 3. REQUIREMENTS In addition, to the requirements listed herei
3、n, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Coun
4、t, +/- 5% tolerance (ASTM D 3887) Wales 134 wales/10 cm Courses 149 courses/10 cm 3.2.2 Fabric Weight, +/- 5%, g/m2(FLTM BN 106-01) Face w/ no Backcoat 316 Laminated to 3 mm foam 445 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Polyester Backcoat No backcoat ENG
5、INEERING MATERIAL SPECIFICATIONWSS-M1H1019-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 20% 16.7 tex f36 (textured yarn) Middle 20% 16.7 texf36 (textured yarn) Back 60% 16.7 tex f36 (textured yarn) 3.5 METHOD OF DYEING Piece Dye 3.6 FINISHING OPERATIONS Knit, Heat set, Setmake, Dye, Tenter dry, Inspect