1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 0 2012 09 06 Released R.Kyle, FoE Controlled document at www.MATS Copyright 2012, Ford Global Technologies, LLC Page 1 of 2 FABRIC, SMITTY TECH, WOVEN JACQUARD, WSS-M1H1153-A1 UNLAMINATED 1. SCOPE The material defined by this specificati
2、on is a dobby woven polyester face fabric containing a PVC effect yarn. 2. APPLICATION This specification was released originally for material used as an interior trim insert fabric for the B299 Individual Program. The fabric was developed as a Tri-Laminate. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS
3、 FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.2 FABRIC CONST
4、RUCTION 3.2.1 Fabric Count, +/- 10 % (ASTM D3775) Warp 100 ends/10 cm Weft 170 picks/10 cm 3.2.2 Fabric Weight, +/- 10 % (FLTM BN 106-01) 500 g/m2 3.3 COMPOSITION (ASTM D629) Fabric 53% PVC / 47% Polyester 3.4 YARN CONSTRUCTION (ASTM D1244) Warp 680dtex f 192 (FTF) 0.8 mm tape PVC 540g/m Weft 680dte
5、x f 192 (FTF) 340dtex f 96 (FTF) ENGINEERING MATERIAL SPECIFICATION WSS-M1H1153-A1 Copyright 2012, Ford Global Technologies, LLC Page 2 of 2 3.5 METHOD OF DYEING Solution dyed or as approved by Materials Engineering 3.6 FINISHED OPERATIONS Washing, Finishing 4. GENERAL INFORMATION The information gi
6、ven below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 Purchase departments will ensure that materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only. 4.2 Global strategy is to use Tri-laminate construction in all regions. 4.3 If yarn is locally sourced it must meet the above fabric construction, Composition & Yarn construction. The fabric must also meet the requirements of WSS-M8P18-A1/A2/A3/A4.