1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2003 04 11 Revised Para 3.0 inserted; Para 3.1, 3.2, 3.3, 3.10, 3.11, 4 deleted 1998 06 29 Activated N.J. Komatsu Printed copies are uncontrolled Page 1 of 2 Copyright 2003, Ford Global Technologies, Inc. FA
2、BRIC, OASIS PATTERN, WARP KNIT, UNLAMINATED WSS-M1H755-A 1. SCOPE The material defined by this specification is a 3 bar 28 gauge warp knitted, simulated velour, polyester bodycloth. 2. APPLICATION WSS-M1H755-A is used for molded set headrests and also adhesive coated for use on inner door panels. 3.
3、 REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Mater
4、ials (WSS-M99P1111-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 8 % tolerance (ASTM D387) Warp 144 wales/10 cm Courses 195 courses/10 cm 3.4.2 Fabric Weight, range (FLTM BN 106-01) 300 +/- 20 g/m23.5 COMPOSITION (ASTM D 629) Fabric 100 % polyester ENGINEERING MATERIAL SPECIFICATION WSS-M1H755
5、-A Page 2 of 2 Copyright 2003, Ford Global Technologies, Inc. 3.6 YARN CONSTRUCTION (ASTM D 1244) Pile 76 dtex f24 (polyester, semi-dul, round) Back 76 dtex f32 (polyester, semi-dul, round) 3.7 METHOD OF DYEING Yarn dyed and spun or as aprovebyMaterials Engineering 3.8 FINISHED OPERATIONS As approve
6、d by Materials Engineering 3.9 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute Note: Not required on face fabric when used as a fully bonded composite. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification: 5.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.