1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2004 01 29 Revised Title revised, para 1, 3.4.1, 3.4.2, 3.5, 3.6, 3.7 and 3.8 revised; para 3.9, 4. and 4.1 added N. J. Komatsu 2003 02 19 Revised Para 3.0 inserted; Para 3.1, 3.2, 3.3, 3.9, 3.10, 4 deleted 1998 03 16 Activated L. Daniv-Zarewy
2、ch Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 1 of 2 FABRIC, KENT PATTERN, PILE KNITTED, WSS-M1H773-A UNLAMINATED 1. SCOPE The material defined by this specification is a 20 gauge, Tricot knit pattern, knit bodycloth of good quality and uniform composition. 2.
3、 APPLICATION This specification was released originally for material used as an interior trim fabric for seats on Sable and Taurus. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/ A2/A3/A4 as applicable. 3.0 STANDARD REQUIREMENTS
4、 FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Europe North American Wales/10cm Courses/10cm 95 102 155 163 98 107
5、 157 - 173 Europe North America 3.4.2 Fabric Weight, range 285 - 325 g/m2387 - 426 g/m2(FLTM BN 106-01) 3.5 COMPOSITION (ASTM D 629) Fabric 100% polyester ENGINEERING MATERIAL SPECIFICATIONWSS-M1H773-APrinted copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 2 of 2 3.6 YARN
6、CONSTRUCTION (ASTM D 1244) Europe North America Face (A) 16.7 tex f48 (polyester, 16.5 tex f47 (polyester semi-dull, round) semi-dull, round) Face (B) 16.7 tex f32 (polyester 16.5 tex 33 (polyester, bright, round) bright, round) Middle 7.6 tex f24 (polyester 11.0 tex f33 (polyester semi-dull, round)
7、 semi-dull, round) Back 7.6 tex f24 (polyester 11.0 tex f33 (polyester semi-dull, round) semi-dull, round) 3.7 METHOD OF DYEING Piece dyed or as approved by Materials Engineering 3.8 FINISHING OPERATIONS As approved by Materials Engineering 3.9 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/
8、minute Note: Not required on face fabric when used as a fully bonded composite. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.