1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2013 04 18 N-Status No Replacement named. A. Reaume, NA 2007 02 08 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.3, 3.17, 3.18 Revised 3.10, 3.11 let flash for 15 minutes, prior to assembly of lap shear) 2024 Alclad Aluminum to 1010 Steel Adhesio
2、n, MPa 0.7 min Joint Movement, mm 1.0 min 2024 Alclad Aluminum to Aluminum Adhesion, MPa 0.7 min Joint Movement, mm 1.0 min ENGINEERING MATERIAL SPECIFICATION WSS-M4G323-A9 Copyright 2013, Ford Global Technologies, LLC Page 4 of 4 3.13.2 Immersion in IRM 902 Oil (168 h at 150+/-2 C) Clean Panels 202
3、4 Alclad Aluminum to 1010 Steel Adhesion, MPa 0.1 min Joint Movement, mm 2.0 min 2024 Alclad Aluminum to Aluminum Adhesion, MPa 0.5 min Joint Movement, mm 1.5 min Oiled Panels: Dip panels in a solution of 5 % IRM 902 oil in toluene; let flash for 15 minutes, prior to assembly of lap shear) 2024 Alcl
4、ad Aluminum to 1010 Steel Adhesion, MPa 0.1 min Joint Movement, mm 2.0 min 2024 Alclad Aluminum to Aluminum Adhesion, MPa 0.5 min Joint Movement, mm 1.5 min 3.14 STORAGE STABILITY, min 10 months (From date of manufacture) When stored in sealed unopened containers out of direct sunlight at ambient te
5、mperatures between 10 & 27 C. The supplier must label each container to indicate expiration date of the material and production usage beyond expiration date is not permitted. Containers should always be kept sealed when not in use. After opening, a plug of cured material may form across the containe
6、r opening during storage. This may easily be removed and does not affect the remaining contents. 3.15 QUALITY The material shall be of uniform quality, free from foreign materials and properties detrimental to normal production use. 3.16 NON-INTERCHANGEABILITY OF MATERIALS Only approved materials all from the same production source shall be used in conjunction with one another.