1、BSI Standards Publication BS ISO 6362-2:2014 Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles Part 2: Mechanical propertiesBS ISO 6362-2:2014 BRITISH STANDARD National foreword This British Standard is the UK implementation of ISO 6362-2:2014. The UK participation in its
2、 preparation was entrusted to Technical Committee NFE/35, Light metals and their alloys. A list of organizations represented on this committee can be obtained on request to its secretary. This publication does not purport to include all the necessary provisions of a contract. Users are responsible f
3、or its correct application. The British Standards Institution 2014. Published by BSI Standards Limited 2014 ISBN 978 0 580 84688 5 ICS 23.040.15; 77.150.10 Compliance with a British Standard cannot confer immunity from legal obligations. This British Standard was published under the authority of the
4、 Standards Policy and Strategy Committee on 30 September 2014. Amendments/corrigenda issued since publication Date Text affected ISO 2014 Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles Part 2: Mechanical properties Aluminium et alliages daluminium corroys Barres, tubes
5、 et profils fils Partie 2: Caractristiques mcaniques INTERNATIONAL STANDARD ISO 6362-2 Fourth edition 2014-09-15 Reference number ISO 6362-2:2014(E)BS ISO 6362-2:2014ISO 6362-2:2014(E)ii ISO 2014 All rights reserved COPYRIGHT PROTECTED DOCUMENT ISO 2014 All rights reserved. Unless otherwise specifie
6、d, no part of this publication may be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below or ISOs
7、member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in SwitzerlandBS ISO 6362-2:2014ISO 6362-2:2014(E) ISO 2014 All rights reserved iii Contents Page Forewor
8、d iv 1 Scope . 1 2 Normative references 1 3 Terms and definitions . 1 4 Tensile testing . 1 5 Mechanical properties 1 Annex A (normative) Rules for rounding 22 Annex B (normative) List of tempers used in Tables 1 to 3 23 Bibliography .25BS ISO 6362-2:2014ISO 6362-2:2014(E) Foreword ISO (the Internat
9、ional Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has bee
10、n established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical stand
11、ardization. The procedures used to develop this document and those intended for its further maintenance are described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the different types of ISO documents should be noted. This document was drafted in accorda
12、nce with the editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives). Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details
13、of any patent rights identified during the development of the document will be in the Introduction and/or on the ISO list of patent declarations received (see www.iso.org/patents). Any trade name used in this document is information given for the convenience of users and does not constitute an endor
14、sement. For an explanation on the meaning of ISO specific terms and expressions related to conformity assessment, as well as information about ISOs adherence to the WTO principles in the Technical Barriers to Trade (TBT) see the following URL: Foreword - Supplementary information The committee respo
15、nsible for this document is ISO/TC 79, Light metals and their alloys, Subcommittee SC 6, Wrought aluminium and aluminium alloys. This fourth edition cancels and replaces the third edition (ISO 6362-2:2012), which has been technically revised. ISO 6362 consists of the following parts, under the gener
16、al title Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles: Part 1: Technical conditions for inspection and delivery Part 2: Mechanical properties Part 3: Extruded rectangular bars Tolerances on shape and dimensions Part 4: Profiles Tolerances on shape and dimensions Part
17、 5: Round, square and hexagonal bars Tolerances on shape and dimensions Part 6: Round, square, rectangular and hexagonal tubes Tolerances on shape and dimensions Part 7: Chemical compositioniv ISO 2014 All rights reservedBS ISO 6362-2:2014INTERNATIONAL ST ANDARD ISO 6362-2:2014(E) Wrought aluminium
18、and aluminium alloys Extruded rods/bars, tubes and profiles Part 2: Mechanical properties 1 Scope This part of ISO 6362 specifies the mechanical properties of wrought aluminium and aluminium alloy extruded rods/bars, tubes, and profiles for general engineering applications. It applies to extruded pr
19、oducts. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including a
20、ny amendments) applies. ISO 6362-1, Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles Part 1: Technical conditions for inspection and delivery ISO 6892-1, Metallic materials Tensile testing Part 1: Method of test at room temperature ASTM B557M, Standard Test Methods for T
21、ension Testing Wrought and Cast Aluminum- and Magnesium- Alloy Products 3 Terms and definitions For the purposes of this document, the terms and definitions given in ISO 6362-1 apply. 4 Tensile testing For the selection of the specimens and tensile testing, see ISO 6892-1 or ASTM B557M. 5 Mechanical
22、 properties Values for mechanical properties of aluminium and aluminium alloys are given in Tables 1 to 3. For elongation, two different gauge lengths are used. The choice of the gauge length for elongation measurements (A or A 50mm ) is at the discretion of the producer, unless otherwise agreed. NO
23、TE A is the percentage elongation on a gauge length of 5,65 S o . A 50mmis the percentage elongation on a gauge length of 50 mm. Test results shall be rounded in accordance with the rules given in Annex A. ISO 2014 All rights reserved 1BS ISO 6362-2:2014ISO 6362-2:2014(E) Table 1 Mechanical properti
24、es of rods/bars Alloy Temper Dimensions a Tensile strength R mMPa 0,2 % proof stress R p0,2MPa Elongation min. min. max. min. max. A % A 50mm% 1070 H112 All 55 15 - 1070A H112 All 60 20 25 23 1060 H112 3 D or S 30 60 30 25 1050 H112 All 65 20 1050A H112 D 35 or S 30 65 20 25 23 O H111 All 60 95 20 2
25、5 23 1350 b H112 All 60 25 23 1100 H112 D 35 or S 30 35 D or 30 S 75 75 20 20 18 18 1200 H112 D 35 or S 30 35 D or 30 S 75 75 25 20 20 18 2007 T4 T4510 T4511 D or S 80 80 D or S 200 200 D or S 250 370 340 330 250 220 210 8 8 7 6 2011 T3 3 D or S 40 40 D or S 50 50 D or S 75 310 295 290 260 235 205 1
26、0 10 10 10 12 14 T4 3 D or S 200 275 125 14 16 T6 3 D or S 75 75 D or S 160 310 295 230 195 8 6 10 8 T8 3 D or S 75 370 275 10 10 2011A T4 D 200, S 60 275 125 14 12 T6 D 75, S 60 75 D 200 310 295 230 195 8 6 6 O c All 250 135 10 12 2014 T4 T4510 T4511 All 345 240 10 12T42 d All 345 205 12T6 T6510 T6
27、511 D or S 12 12 D or S 19 19 D or S, A 16 000 19 D or S, 16 000 A 20 000 19 D or S, 20 000 A 25 000 19 D or S, 25 000 A 30 000 410 440 470 470 450 430 365 400 410 400 380 365 6 6 6 6 6 7 7 7 6 6 6T62 e D or S 19 19 D or S, A 16 000 19 D or S, 16 000 A 20 000 410 410 410 365 365 365 7 7 62 ISO 2014
28、All rights reservedBS ISO 6362-2:2014ISO 6362-2:2014(E) Alloy Temper Dimensions a Tensile strength R mMPa 0,2 % proof stress R p0,2MPa Elongation min. min. max. min. max. A % A 50mm% 2014A O 10 D or S 200 250 135 10 12 T4, T4510 T4511 10 D or S 200 345 240 10 12 T6 T6510 T6511 12,5 D or S 100 100 D
29、or S 120 120 D or S 200 440 430 430 400 350 350 6 6 6 2017 O c All 245 125 - 16 T4 T42 d A 70 000 70 000 A 100 000 345 345 215 195 12 12 2017A O 10 D or S 100 250 150 10 T4 T4510 T4511 10 D or S 80 80 D or S 200 390 360 265 220 10 7 O c All 245 125 10 12T3510 T3511 D or S 6 6 D or S 19 19 D or S 38
30、38 D or S, A 16 000 38 D or S, 16 000 A 20 000 390 410 450 480 470 295 300 310 365 335 10 8 7 7 12 12 10 10 8 2024 T3 T4 D or S 6 6 D or S 19 19 D or S 38 38 D or S 100, A 16 000 38 D or S 100, 16 000 A 20 000 38 D or S 100, 20 000 A 30 000 100 D or S 200, A 16 000 100 D or S 200, 16 000 A 20 000 10
31、0 D or S 200, 20 000 A 30 000 390 410 450 480 470 460 480 470 460 295 305 315 365 335 315 365 335 315 8 8 8 6 6 6 12 12 10 10 8 8 10 8 8T42 d D or S 19 19 D or S 38 38 D or S, A 16 000 38 D or S, 16 000 A 20 000 390 390 390 390 265 265 265 265 12 10 10 8T8510 T8511 T81 10 D or S 150 455 400 4 2030 T
32、4 T4510 T4511 D or S 80 80 D or S 200 200 D or S 250 370 340 330 250 220 210 8 8 7 6 Table 1 (continued) ISO 2014 All rights reserved 3BS ISO 6362-2:2014ISO 6362-2:2014(E) Alloy Temper Dimensions a Tensile strength R mMPa 0,2 % proof stress R p0,2MPa Elongation min. min. max. min. max. A % A 50mm% 3
33、102 H112 All 80 30 25 23 3003 H112 All 95 35 O H111 All 95 135 35 25 20 3103 H112 All 95 35 25 20 O H111 All 95 135 35 25 20 5005 5005A H112 All 100 40 18 16 O H111 D 80, S 60 100 150 40 18 16 5019 H112 D or S 200 250 110 14 12 O H111 D or S 200 250 320 110 15 13 5049 H112 All 180 80 15 13 5051A H11
34、2 All 150 50 16 14 O H111 All 150 200 50 18 16 5251 H112 All 160 60 16 14 O H111 All 160 220 60 17 15 5052 H112 All 175 70 O All 175 245 70 20 5154A H112 D or S 200 200 85 16 14 O H111 D or S 200 200 275 85 18 16 5454 H112 All 215 100 12 O H111 D or S 200 200 275 85 18 16 5754 H112 D or S 150 150 D
35、or S 250 180 180 80 70 14 13 12 O H111 D or S 150 180 250 80 17 15 5056 H112 A 30 000 30 000 A 70 000 70 000 A 100 000 245 225 215 100 80 70 5083 H112 D or S 130, A 20 000 275 140 12 12 O D or S 130, A 20 000 275 355 110 14 5086 H112 D or S 250 240 95 12 10 O D or S 200 240 320 95 18 15Table 1 (cont
36、inued) 4 ISO 2014 All rights reservedBS ISO 6362-2:2014ISO 6362-2:2014(E) Alloy Temper Dimensions a Tensile strength R mMPa 0,2 % proof stress R p0,2MPa Elongation min. min. max. min. max. A % A 50mm% 6101 T6 f 3 D or S 7 7 D or S 17 17 D or S 30 195 195 175 165 165 145 10 12 14 T7 3 D or S 17 135 1
37、10 10 6101A T6 f D or S 150 200 170 10 8 6101B T6 f,g S 15 215 160 8 6 T7 f,h S 15 170 120 12 10 6005 6005A T6 f D or S 25 25 D or S 50 50 D or S 100 270 270 260 225 225 215 10 8 8 8 6005C T5 D or S 6 6 D or S 12 245 225 205 175 8 8 T6 f D or S 6 265 235 8 6110A T5 f D or S 120 380 360 10 8 T6 f D 1
38、20 or S 150 410 380 10 8 6012 T6 f T6510 f T6511 f D or S 150 150 D or S 200 310 260 260 200 8 8 6 6018 T6 f T6510 f T6511 f D or S 150 150 D or S 200 310 260 260 200 8 8 6 6023 T6 f T6510 f T6511 f D or S 150 320 270 10 8 6351 O H111 D or S 200 160 110 14 12 T4 f D or S 200 205 110 14 12 T6 f D or
39、S 20 20 D or S 75 75 D or S 150 150 D or S 200 200 D or S 250 295 300 310 280 270 250 255 260 240 200 8 8 8 6 6 6 6060 T4 f D or S 150 120 60 16 14 T5 D or S 150 160 120 8 6 T6 f D or S 100 190 150 10 8 T64 f D or S 50 180 120 12 10 T66 f D or S 150 215 160 8 6Table 1 (continued) ISO 2014 All rights
40、 reserved 5BS ISO 6362-2:2014ISO 6362-2:2014(E) Alloy Temper Dimensions a Tensile strength R mMPa 0,2 % proof stress R p0,2MPa Elongation min. min. max. min. max. A % A 50mm% 6360 T4 f D or S 150 110 50 16 14 T5 D or S 150 150 110 8 6 T6 f D or S 150 185 140 8 6 T66 f D or S 150 195 150 8 6 6061 O c
41、 All 145 110 16 T4 f T4511 All 180 110 14 16 T42 d All 175 85 16 T6 f T62 e T6511 D or S 6 6 D or S 260 260 240 240 7 9 8 10 6261 O H111 D or S 100 170 120 14 12 T4 f D or S 100 180 100 14 12 T6 f D or S 20 20 D or S 100 290 290 245 245 8 8 7 6262 T6 f D or S 200 260 240 10 8 6262A T6 f D 220 or S 1
42、55 260 240 10 8O H111 D or S 200 130 18 16T1 D or S 12 12 D or S 25 120 110 60 55 12 12 6063 T4 f D or S 150 150 D or S 200 130 120 65 65 14 12 12 T5 D or S 12 12 D or S 25 150 145 110 105 7 7 8 8T6 f D or S 3 3 D or S 25 205 205 170 170 9 8 10T66 f D or S 200 245 200 10 8O H111 D or S 200 150 16 14
43、 6063A T4 f D or S 150 150 D or S 200 150 140 90 90 12 10 10 T5 D or S 200 200 160 7 5T6 f D or S 150 150 D or S 200 230 220 190 160 7 7 5 6463 T4 f D or S 150 125 75 14 12 T5 D or S 150 150 110 8 6 T6 f D or S 150 195 160 10 8Table 1 (continued) 6 ISO 2014 All rights reservedBS ISO 6362-2:2014ISO 6
44、362-2:2014(E) Alloy Temper Dimensions a Tensile strength R mMPa 0,2 % proof stress R p0,2MPa Elongation min. min. max. min. max. A % A 50mm% 6065 T6 f D 220 or S 155 260 240 10 8 6081 T6 f D or S 250 275 240 8 6 6082 O H111 D or S 200 160 110 14 12 T4 f 10 D or S 80 205 110 14 14 T6 f 10 D 60 or 10
45、S 50 60 D 150 or 50 S 150 310 300 260 240 8 8 7 6182 T4 f D 220 or S 155 205 110 12 10 T6 f,i 9 D or S 100 100 D or S 150 150 D or S 220 360 330 280 330 300 240 9 8 6 7 6 4 7003 T5 D or S 12 12 D or S 25 285 275 245 235 10 10 T6 f D or S 50 50 D or S 150 350 340 290 280 10 10 8 8 7204 O All 245 145 12 T4 j All 315 195 11 T6 All 335 275 10 7005 T6 f D or S 50 50 D or S 200 350 340 290 270 10 10 8 7108 T6 f D or S 100 310 260 10 8 7108A T6 f D or S 200 310 260 12 10