1、ASD STANDARD NORME ASD ASD NORM prEN 4632-003 Edition P 1 December 2008 PUBLISHED BY THE AEROSPACE AND DEFENCE INDUSTRIES ASSOCIATION OF EUROPE - STANDARDIZATIONAvenue de Tervuren, 270 - B-1150 Brussels - Tel. + 32 2 775 8126 - Fax. + 32 2 763 3565 - www.asd-stan.orgICS: Descriptors: ENGLISH VERSION
2、 Aerospace series Weldability and brazeability of materials in aerospace constructions Part 003: Homogeneous assemblies of unalloyed and low alloy steels Srie arospatiale Soudabilit et brasabilit des matriaux pour constructions arospatiales Partie 003 : Assemblages homognes des aciers non allis et f
3、aiblement allis Luft- und Raumfahrt Schweibarkeit und Ltbarkeit von Werkstoffen im Luft und Raumfahrzeugbau Teil 003: GleicharGTAW e Verbindungen unlegierten und niedriglegierten Stlhen This “Aerospace Series“ Prestandard has been drawn up under the responsibility of ASD-STAN (The AeroSpace and Defe
4、nce Industries Association of Europe - Standardization). It is published for the needs of the European Aerospace Industry. It has been technically approved by the experts of the concerned Domain following member comments. Subsequent to the publication of this Prestandard, the technical content shall
5、 not be changed to an extent that interchangeability is affected, physically or functionally, without re-identification of the standard. After examination and review by users and formal agreement of ASD-STAN, it will be submitted as a draft European Standard (prEN) to CEN (European Committee for Sta
6、ndardization) for formal vote and transformation to full European Standard (EN). The CEN national members have then to implement the EN at national level by giving the EN the status of a national standard and by withdrawing any national standards conflicting with the EN. Edition approved for publica
7、tion 31 December 2008 Comments should be sent within six months after the date of publication to ASD-STAN Metallic Material Domain Copyright 2008 by ASD-STAN prEN 4632-003:20082 Contents Page Foreword2 1 Scope 3 2 Normative references3 3 Terms and definitions .6 4 Use of this standard 6 5 Updating t
8、his standard7 6 Index of steel sheets .7 7 Material sheets.8 Bibliography30 Foreword This standard was reviewed by the Domain Technical Coordinator of ASD-STANs Metallic Material Domain. After inquiries and votes carried out in accordance with the rules of ASD-STAN defined in ASD-STANs General Proce
9、ss Manual, this standard has received approval for Publication. prEN 4632-003:2008 3 1 Scope This standard defines degrees of weldability and brazeability for materials or families of materials used in the aerospace industry. It comprises a series of sheets, by materials or by material families, whi
10、ch: indicate the main titles, the typical chemical composition and the main characteristics, contain recommendations for welding and brazing, indicate a degree of weldability or brazeability for a given process under defined conditions, indicate a value of the mechanical strength coefficient of the
11、welded joint for each welding process, when it could be extracted from bibliographic references referring to it. The joint coefficient is expressed as a ratio of the tensile strength of the welded joint to the tensile strength of the base alloy. To define preheating conditions, it recommends ISO TR
12、17671-2 recommendations. These conditions depend on the calculation of carbon equivalent, welding energy per unit length, thickness, arc welding process and hydrogen rate in filler metal. It is applicable without restriction for the manufacturing of new parts or for repair. 2 Normative references Th
13、e following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 636, Welding consumables Rods, wires and deposi
14、ts for tungsten inert gas welding of non-alloy and unalloyed and low alloy steels Classification. EN ISO 4063, Welding and allied processes Nomenclature of processes and reference numbers. ISO/TR 17671-2, Welding Recommendations for welding of metallic materials Part 2: Arc welding of ferritic steel
15、s. EN 439, Welding consumables Shielding gases for arc welding and cutting. EN 440, Welding consumables Wire electrodes and deposits for gas shielded metal arc welding of non alloy and fine grain steels Classification. EN 499, Welding consumables Covered electrodes for manual metal arc welding of no
16、n alloy and fine grain steels Classification. EN 758, Welding consumables Tubular cored electrodes for metal arc welding with and without a gas shield of non alloy and fine grain steels Classification. EN 1045, Brazing Fluxes for brazing Classification and technical delivery conditions. EN 1599, Wel
17、ding consumables Covered electrodes for manual metal arc welding of creep-resisting steels Classification. prEN 4632-003:20084 EN 2135, Aerospace series Steel FE-PL61 Carburized, hardened and tempered Bar De 40 mm. 1)EN 2213, Steel FE-PL52 S 980 MPa Rm 1 180 MPa Bars De 16 mm Aerospace series. 1) EN
18、 2218, Steel FE-PL52 S 980 MPa Rm 1 180 MPa Tubes for structures a 4 mm d 5 a Aerospace series. 1)EN 2220, Steel FE-PL52 S 1 080 MPa Rm 1 250 MPa Tubes for structures 2 mm a 20 mm d 5 a Aerospace series. 1)EN 2767, Aerospace series Steel FE-PL79 Carburized, hardened and tempered 1180 Rm 1550 MPa Bar
19、 for machining De 150 mm. 1)EN 2768, Aerospace series Steel FE-PL79 Carburized, hardened and tempered 1180 Rm 1550 MPa Forgings De 150 mm. EN 2779, Aerospace series Steel FE-PL56 Hardened and tempered 1250 Rm 1400 MPa Bars De 70 mm. EN 2780, Aerospace series Steel FE-PL56 Hardened and tempered 1250
20、Rm 1400 MPa Forgings De 70 mm. EN 3522, Aerospace series Steel FE-PL79 Softened Reference heat treatment: carburized, hardened and tempered Forging stock De 200 mm. EN 3523, Aerospace series Steel FE-PL1505 (15CrMoV6) Air melted Hardened and tempered Bar for machining De 100 mm 1 080 MPa Rm 1 280 MP
21、a. 1)EN 3524, Aerospace series Steel FE-PL1505 (15CrMoV6) Air melted Hardened and tempered Bar for machining 2 mm a 6 mm 1 080 MPa Rm 1 280 MPa. EN 3525, Aerospace series Steel FE-PL1505 (15CrMoV6) Air melted Hardened and tempered Plate 6 mm 12 Normalized Stress relieving if necessary 1 Basic covere
22、d electrodes E 42B according to EN 499 4 Normalized 1 1 Filler metal: Steel for GTAW with Si + Mn(type G3Si1 according to EN 440) GTAW 141 4 (1strun) Normalized none 1 Ditto GMAW 135, GMAW 136 all Normalized none 1 1 Solid welding wire G3Si1 grade according to EN 440 Recommended gas: CO2(C1 accordin
23、g to EN 439 ) or CO2+ Ar mixture (M2-1 according to EN 439 ) Tubular cored electrode according to EN 758 (T ) RSEW 22, RSW 21 all Normalized none 1 RFW 24 all Normalized or as rolled Normalized 1 Recommendations for brazing and assemblies by diffusion Filler metal Process EN ISO 4063 reference numbe
24、r State before joining Joining temperature C PJHT family form Flux Degree of brazeabilityor weldability Comments Normalized 1083 Cu F, w tp * 1 * flux: dissociated ammonia Normalized 620 Ag (40 %) F, w tp * 1 * FH10 flux according to EN 1045B 91 Normalized 750 Ag (20 %) F, w tp * 1 * FH10 flux accor
25、ding to EN 1045BW 97 Normalized 950 Cu + Zn F * 1 * covered rods or FH20 flux according to EN 1045+ bare brass rods (B/SB Cu 59 Zn Si 870-890) prEN 4632-003:200810 7.2 Designation: EN 10025 : S 235, S 275 Current : Steel for general use in metallic construction ASD STAN : Other standards : Typical c
26、hemical composition (w.%): Steel grade Fe Si Mn S235 base 1,5 S275 base 1,6 Structure: Particular characteristics: Analyses on heats for S235 grades with thicknesses less than 16 mm. Designation C % P % S % Minimum impact energy a at S235JRG2 S235J0 S235J2G3 0,17 0,17 0,17 0,045 0,040 0,035 0,045 0,
27、040 0,030 20 C 0 C 20 C aV notch impact. Analyses on heats for S275 grades with thickness less than 16 mm. Designation C % P % S % Minimum impact energy a at S275JR S275J0 S275J2G3 0,21 0,18 0,18 0,045 0,040 0,035 0,045 0,040 0,035 20 C 0 C 20 C aV notch impact. Forms: Sheets, commercial rolled, bea
28、ms, wide flats, foils, hot rolled. Particular comments: Welding of effervescent steel, in particular S235JR, S235JRG1 steels, shall be avoided. prEN 4632-003:2008 11 Recommendations for welding and filling S235 and S275 steels Process EN ISO 4063 reference number Thickness range mm State before weld
29、ing PWHT Degree of weldability Joint efficiency Comments and bibliographic references OAW 311 6 none 1 Filler metal: G3Si1 according to EN 440 12 none 1 1 Rutile covered electrodes E 35R according to EN 499 SMAW 111 12 Stress relieving if necessary 1 Basic covered electrodes E 42B according to EN 49
30、9 4 none 1 1 Filler metal: Steel for GTAW with Si + Mn (G3Si1 type according to EN 440) GTAW 141 4 (1strun) none 1 1 Ditto GMAW 135, GMAW 136 all Preheating according to ISO/ TR 17671-2 for thickness 15 mm none 1 1 Solid welding wire G3Si1 grade according to EN 440 gas recommended: CO2(C1 according
31、to EN 439) or CO2+ Ar mixture (M2-1 according to EN 439) Tubular cored electrode according to EN 758 (T ) RSEW 22, RSW 21 all Normalized none 1 RFW 24 all Normalized Normalized 1 Recommendationsfor brazing and assemblies by diffusion Filler metal Process EN ISO 4063 reference number State before joi
32、ning Joining temperature C PJHT family form Flux Degree of brazeability or weldability Comments 1083 Cu F, w tp * 1 * flux: dissociated ammonia 620 Ag (40 %) F, w tp * 1 * FH10 flux according to EN 1045B 91 750 Ag (20 %) F, w, tp * 1 * FH10 flux according to EN 1045BW 97 950 Cu + Zn F * 1 * covered
33、rods or FH20 flux according to EN 1045 + bare brass rods (B/SB Cu 59 Zn if 870-890) prEN 4632-003:200812 7.3 Designation: EN 10025 : S355 Current : steel for general use in metallic construction ASD STAN : Other standards : Typical chemical composition (w.%): Steel grade Fe Si % Mn % S355 base 0,55
34、1,60 Structure: Particular characteristics: Analyses on heats for S 355 grades with thickness less than 16 mm. Designation C % P % S % Minimum impact energy a at S355JR S355J0 S275K2G3 0,24 0,20 0,20 0,045 0,040 0,035 0,045 0,040 0,035 20 C 0 C 20 C aV notch impact. Forms: Sheets, commercial rolled,
35、 beams, wide flats, foils, hot rolled. prEN 4632-003:2008 13 Recommendations for welding and filling of S355 steels Process EN ISO 4063 reference number Thickness range mm State before welding PWHT Degree of weldability Joint efficiency Comments and bibliographic references OAW 311 6 Normalized none
36、 1 Filler metal: G3Si1 according to EN 440 SMAW 111 all Normalized Stress relieving if necessary 1 1 Basic covered electrodes E 42 4 B according to EN 499 4 Normalized none 1 1 GTAW 141 4 (1strun) Normalized none 1 Filler metal: GTAW with Si + Mn (G3Si1 grade according to EN 440) GMAW 135, GMAW 136
37、all Pre heating ISO/ TR 17671-2 for thickn-ess 15 mm Stress relieving at 590 C if necessary 1 1 Solid welding wire G3Si1 grade according to EN 440 Recommended gas: CO2(C1 according to EN 439) or CO2+ Ar mixture (M2-1 according to EN 439) Tubular cored electrode according to EN 758 (T ) RSEW 22, RSW
38、21 all Normalized none 1 RFW 24 all Normalized Normalized 1 Recommendations for brazing and assemblies by diffusion Filler metal Process EN ISO 4063 reference number State before joining Joining temperature C PJHT family form Flux Degree of brazeability or weldability Comments Normalized 1083 Cu F,
39、w tp * 1 * flux: dissociated ammonia Normalized 620 Ag (40 %) F, w Tp * 1 * FH10 flux according to EN 1045B 91 Normalized 750 Ag (20 %) F, w tp * 1 * FH10 flux according to EN 1045BW 97 Normalized 950 Cu + Zn F * 1 * covered rods or FH20 flux according to EN 1045 + bare brass rods (B/SB Cu 59 Zn Si
40、870-890) prEN 4632-003:200814 7.4 Designation: EN 10083-1 : C22E Current : unalloyed structural steel for heat treatment ASD STAN : Other standards : AISI: 1017-1020 Typical chemical composition (w.%): (from heat) Steel grade Fe C Mn Si S P Cr Mo Ni Cr+Mo+NiC22E base 0,17to 0,24 0,4 to 0,70 0,40 0,0
41、35 0,035 0,40 0,10 0,40 0,63 Structure: Particular characteristics: Forms: Sheets, wide flats, semi-products, bars, wire. prEN 4632-003:2008 15 Recommendations for welding and filling of C22E steel Process EN ISO 4063 reference number Thickness range mm State before welding PWHT Degree of weldabilit
42、yJoint efficiency Comments and bibliographic references OAW 311 6 Annealed none 1 Filler metal: G3Si1 according to EN 440 SMAW 111 all Annealed Stress relieving 1 Basic covered electrodes E 42 4 B according to EN 499 4 Annealed none 1 GTAW 141 4 (1strun) Annealed none 1 Filler metal: GTAW with Si +
43、Mn G3Si1 grade, according to EN 440 GMAW 135, GMAW 136 all Annealed none 1 Solid welding wire according to G3Si1 grade according to EN 440 Recommended gas: CO2or CO2+ Ar mixture Tubular cored electrode according to EN 758 (TGS ) EBW 51 Annealed none 1 1 GLW 522 6 Annealed none 1 1 CDFW 42 4 As forge
44、d none 1 1 RSEW 22, RSW 21 all Normalized none 1 RFW 24 all Normalized Normalized 1 Recommendations for brazing and assemblies by diffusion Filler metal Process EN ISO 4063 reference number State before joining Joining temperature C PJHT family form Flux Degree of brazeability or weldability Comment
45、s Tempered 1083 Cu F, w tp * 1 * flux: dissociated ammonia Tempered 620 Ag (40 %) F, w tp * 1 * FH10 flux according to EN 1045B 91 Tempered 750 Ag (20 %) F, w tp * 1 * FH10 flux according to EN 1045BW 97 Tempered 950 Cu + Zn F * 1 * covered rods or FH20 flux according to EN 1045 + bare brass rods (B
46、/SB Cu 59 Zn Si 870-890) prEN 4632-003:2008 16 7.5 Designation: EN 2135, EN 2767, EN 2768, EN 3522 : 12NiCr12, 16NiCrMo17 EN 10084 : 20NiCrMo6-4 Current : 12NCD12, 16NCD17 ASD STAN : FE-PL 2101, FE-PL 2110 Other standards : 16NiCrMo13 Typical chemical composition (w.%): Steel grade Fe C Mn Si Ni Cr
47、Mo 12NiCr12 base 0,1 to 0,16 0,35 to 0,65 0,15 to 0,40 2,75 to 3,25 0,60 to 0,90 16NiCrMo17 base 0,14 to 0,18 0,35 to 0,45 0,10 to 0,30 4,0 to 4,5 1 to 1,3 0,15 to 0,35 16NiCrMo13 base 0,12 to 0,17 0,30 to 0,60 0,15 to 0,40 3,00 to 3,50 0,90 to 1,20 0,15 to 0,30 20NiCrMo6-4 base 0,16 to 0,23 0,50 to
48、 0,90 0,40 1,40 to 1,70 0,60 to 0,90 0,25 to 0,35 Structure: Particular characteristics: Steels intended for subsequent heat treatments: Carburizing followed by quenching and tempering; Quenching and tempering. These steels shall be welded before carburizing or on no carburized areas protected during carburizing. prEN 4632-003:2008 17 Recommen