ASTM B443-2000(2009) Standard Specification for Nickel-Chromium-Molybdenum-Columbium Alloy (UNS N06625) and Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219) Plate Sheet and St.pdf
《ASTM B443-2000(2009) Standard Specification for Nickel-Chromium-Molybdenum-Columbium Alloy (UNS N06625) and Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219) Plate Sheet and St.pdf》由会员分享,可在线阅读,更多相关《ASTM B443-2000(2009) Standard Specification for Nickel-Chromium-Molybdenum-Columbium Alloy (UNS N06625) and Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219) Plate Sheet and St.pdf(8页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: B 443 00 (Reapproved 2009)Standard Specification forNickel-Chromium-Molybdenum-Columbium Alloy(UNS N06625) and Nickel-Chromium-Molybdenum-SiliconAlloy (UNS N06219)* Plate, Sheet, and Strip1This standard is issued under the fixed designation B 443; the number immediately following the de
2、signation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use
3、by agencies of the Department of Defense.1. Scope1.1 This specification2covers rolled nickel-chromium-molybdenum-columbium alloy (UNS N06625) and nickel-chromium-molybdenum-silicon alloy (UNS N06219)* plate,sheet, and strip.1.1.1 Alloy UNS N06625 products are furnished in twogrades of different heat
4、-treated conditions:1.1.1.1 Grade 1 (Annealed)Material is normally em-ployed in service temperatures up to 1100F (593C).1.1.1.2 Grade 2 (Solution Annealed)Material is normallyemployed in service temperatures above 1100F (593C) whenresistance to creep and rupture is required.NOTE 1Hot-working or rean
5、nealing may change properties signifi-cantly, depending on working history and temperatures.1.1.2 Alloy UNS N06219 is supplied in solution annealedcondition only.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI
6、 units that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in
7、 the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3B 446 Specification for Ni
8、ckel-Chromium-Molybdenum-Columbium Alloy (UNS N06625), Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219), and Nickel-Chromium-Molybdenum-Tungsten Alloy (UNS N06650)*Rod and BarB 880 Specification for General Requirements for ChemicalCheck Analysis Limits for Nickel, Nickel Alloys andCobalt Alloy
9、sE8 Test Methods for Tension Testing of Metallic MaterialsE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE 1473 Test Methods for Chemical Analysis of Nickel,Cobalt, and High-Temperature Alloys3. Terminology3.1 Definitions of Terms Specific to This S
10、tandard: Theterms given in Table 1 shall apply.4. Ordering Information4.1 It is the responsibility of the purchaser to specify allrequirements that are necessary for the safe and satisfactoryperformance of material ordered under this specification.Examples of such requirements include, but are not l
11、imited to,the following:4.1.1 ASTM designation,4.1.2 Alloy name or UNS number,4.1.3 ConditionSee 1.1.1, 1.1.2 and Appendix X1,4.1.3.1 If neither grade of N06625 is specified, Grade 1 willbe supplied,4.1.4 FinishAppendix X1,4.1.5 DimensionsThickness, width, and length,1This specification is under the
12、 jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved Oct. 1, 2009. Published October 2009. Originallyapproved in 1966. Last previous edition approved in 2005 as
13、 B 443 - 00 (2005).2For ASME Boiler and Pressure Vessel Code applications, see related Specifi-cation SB-443 in Section II of that Code.* New designation established in accordance with Practice E 527 and SAEJ1086, Practice for Numbering Metals and Alloys (UNS).3For referenced ASTM standards, visit t
14、he ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,
15、 United States.4.1.6 Quantity,4.1.7 Optional Requirements:4.1.7.1 Sheet and StripWhether to be furnished in coil, incut straight lengths, or in random straight lengths,4.1.7.2 PlateHow plate is to be cut (see 7.2.1 and 7.3.2),4.1.8 CertificationState if certification is required (Sec-tion 15),4.1.9
16、Samples for Product (Check) AnalysisWhethersamples for product (check) analysis should be furnished (see5.2), and4.1.10 Purchaser InspectionIf the purchaser wishes towitness tests or inspection of material at place of manufacture,the purchase order must so state, indicating which tests orinspections
17、 are to be witnessed (Section 13).5. Chemical Composition5.1 The material shall conform to the composition limitsspecified in Table 2.5.2 If a product (check) analysis is performed by thepurchaser, the material shall conform to the product (check)analysis variations as prescribed by Specification B
18、880.6. Mechanical Properties and Other Requirements6.1 Mechanical PropertiesThe material shall conform tothe heat treatment and room temperature tensile propertiesprescribed in Table 3.7. Dimensions and Permissible Variations7.1 Thickness and Weight:7.1.1 PlateFor plate up to 2 in. (50.8 mm), inclus
19、ive, inthickness, the permissible variations under the specified thick-ness and permissible excess in overweight shall not exceed theamounts prescribed in Table 4.7.1.1.1 For use with Table 4, plate shall be assumed toweigh 0.305 lb/in.3(8.442 g/cm3).7.1.2 PlateFor plate over 2 in. (50.8 mm) in thic
20、kness, thepermissible variations over the specified thickness shall notexceed the amounts prescribed in Table 5.7.1.3 Sheet and StripThe permissible variations in thick-ness of sheet and strip shall be as prescribed in Table 6. Thethickness of strip and sheet shall be measured with themicrometer spi
21、ndle38 in. (9.5 mm) or more from either edgefor material 1 in. (25.4 mm) or over in width and at any placeon the strip under 1 in. (25.4 mm) in width.7.2 Width or Diameter:7.2.1 PlateThe permissible variations in width of rectan-gular plates and diameter of circular plates shall be asprescribed in T
22、able 7 and Table 8.7.2.2 Sheet and StripThe permissible variations in widthfor sheet and strip shall be as prescribed in Table 9.7.3 Length:7.3.1 Sheet and strip of all sizes may be ordered to cutlengths, in which case a variation of18 in. (3.2 mm) over thespecified length shall be permitted.7.3.2 P
23、ermissible variations in length of rectangular plateshall be as prescribed in Table 10.7.4 Straightness:7.4.1 The edgewise curvature (depth of chord) of flat sheet,strip, and plate shall not exceed 0.05 in. (1.27 mm) multipliedby the length in feet (0.04 mm multiplied by the length incentimetres).7.
24、4.2 Straightness for coiled material is subject to agree-ment between the manufacturer and the purchaser.7.5 Edges:7.5.1 Sheet and strip shall have sheared or slit edges.7.5.2 Plate shall have sheared or cut (machined, abrasivecut, powder cut, or inert arc cut) edges, as specified.7.6 Squareness (Sh
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
本资源只提供5页预览,全部文档请下载后查看!喜欢就下载吧,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMB44320002009STANDARDSPECIFICATIONFORNICKELCHROMIUMMOLYBDENUMCOLUMBIUMALLOYUNSN06625ANDNICKELCHROMIUMMOLYBDENUMSILICONALLOYUNSN06219PLATESHEETANDSTPDF

链接地址:http://www.mydoc123.com/p-461249.html