1、Designation: C1635 16Standard Test Method toEvaluate Adhesion/Cohesion Properties of a Sealant atFixed Extension1This standard is issued under the fixed designation C1635; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of
2、 last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method describes a laboratory procedure formeasuring the adhesion/cohesion properties of a sealant whensubj
3、ected to tensile loads resulting from an applied specifiedstrain. The adhesion/cohesion properties are evaluated before,during, and after water immersion.1.2 This test method examines the adhesive and cohesiveperformance of a sealant on a specified substrate at a strainequivalent to a multiple of th
4、e strain/movement capabilitydesignated by the manufacturer for the given sealant perSpecification C920.1.3 The values stated in SI (metric) units are to be regardedas the standard. The inch values given in parentheses are forinformation only.1.4 This standard does not purport to address all of thesa
5、fety concerns, if any associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.1.5 Comparable Test:1.5.1 ISO 10590, Building construction - Jointing prod
6、ucts- Sealants - Determination of adhesion/cohesion properties atmaintained extension after immersion in water1.5.2 ISO 8340, Building construction - Jointing products -Sealants - Determination of tensile properties at maintainedextension2. Referenced Documents2.1 ASTM Standards:2C717 Terminology of
7、 Building Seals and SealantsC719 Test Method for Adhesion and Cohesion of Elasto-meric Joint Sealants Under Cyclic Movement (HockmanCycle)C920 Specification for Elastomeric Joint SealantsC1375 Guide for Substrates Used in Testing Building Sealsand Sealants3. Terminology3.1 DefinitionsRefer to Termin
8、ology C717 for definitionsof terms used in this standard, including but not limited to thefollowing: adhesive failure, casting spacers, cohesive failure,standard conditions.3.2 separatorsthe device or item used to maintain thespecimens at fixed extension.4. Summary of Test Method4.1 Test specimens m
9、ade in accordance with dimensions setforth in Test Method C719 are fabricated and allowed to cure.4.2 Test specimens are extended at standard conditions asdefined in Terminology C717 to a specified strain and blockedat the strain for a specified period of time.4.3 The test specimens are examined for
10、 adhesive or cohe-sive failure, or both, of the sealant at 0, 24 and 168 h.4.4 A duplicate set of three test specimens are cured atstandard conditions as defined in Terminology C717, extendedto a specified strain, and then immersed (totally) in deionizedwater or specified medium (3 specimens/liter o
11、f liquid).4.5 Immersed test specimens are observed at 0, 24 and 168and other additional specified hours.4.6 This test method uses ASTM standard substrates asdescribed in Guide C1375. This test method does not excludethe use of any other substrate that provides a suitable flatsurface.5. Significance
12、and Use5.1 In any sealant application, the sealant must be capable ofmaintaining an adhesive bond to the substrate when held instrain for its intended service life.5.2 This test method is an indicator of a sealants ability toadhere under strain to a given substrate.1This test method is under the jur
13、isdiction ofASTM Committee C24 on BuildingSeals and Sealants and is the direct responsibility of Subcommittee C24.30 onAdhesionCurrent edition approved June 1, 2016. Published July 2016. Originally approvedin 2006. Last previous edition approved in 2014 as C1635-14. DOI: 10.1520/C1635-16.2For refere
14、nced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West C
15、onshohocken, PA 19428-2959. United States15.3 The default test strain is the movement ability of thesealant as designated by the manufacturer. The default jointconfiguration is 12.7 12.7 50.8 mm (12 12 2 in.). Otherstrains and joint configurations may be used and reported asnoted in Section 8 and Ta
16、ble 1.6. Apparatus and Materials6.1 Container, for immersion made of a material compatiblewith the immersion medium.6.2 Device, to provide a strain on the test specimen.6.3 Spatulas, for use in applying the sealant.6.4 Caulking Gun, for extruding sealant from cartridgeswhen applicable.6.5 Substrates
17、Twelve substrates minimum of 25.4 76.2mm (1 3 in.) of the same finish are required for each testsample.6.6 Casting SpacersMade from polytetrafluoroethylene(PTFE) or a suitable rigid material shall be used with each testspecimen to which the test sealant will not bond and willprovide the appropriate
18、joint dimensions and configurations.6.7 Substrate Cleaning Materials:6.8 Primer (if needed).6.9 Separators, to provide a constant strain on the specimenwhilst maintaining parallel bond surfaces.6.10 Deionized Water, or other specified liquid medium forimmersion6.11 Suitable Probe Type Measuring Devi
19、ce, capable ofmeasuring defects in the sealant to 1 mm (132 in.)7. Procedure7.1 Preparation of Test Specimens. Six test specimens.7.1.1 Standard conditions of temperature and relative hu-midity used throughout this test method are defined as inTerminology C717.7.1.2 Clean the substrates per the proc
20、edures set forth inTest Method C719 and Guide C1375.7.1.3 PrimersWhere use of primer is recommended by thesealant manufacturer, substrate materials shall be primed withthe recommended primer or primers.7.1.4 Apply a bead of sealant 12.7 12.7 50.8 mm (12 12 2 in.) between parallel 25.4 76.2 mm (1 3 i
21、n.)substrates (or of other desired dimensions and noted in thereport). Use appropriate casting spacers to form the proper sizebead. Use adhesive tape, rubber bands, or clamps to hold thetest assembly together before and after filling it with thesealant. In the case of a pourable-type sealant, use ma
22、sking orany other suitable tape to retain the sealant. Use masking tapeon top surface of substrates to prevent sealant from curing onthe top surface. Remove the tape immediately following fillingthe specimen joint cavity.7.2 Curing Method:7.2.1 Cure specimens under one of the following cycles:7.2.1.
23、1 Standard ConditionsAs defined in TerminologyC717 for a minimum of 21 days.7.2.1.2 Alternately, cure for a total of 21 days as follows: (a)7 days at standard conditions above; (b) 7 days at 38 6 2C(100 6 3.6 F) and 95 % relative humidity; (c) 7 days atstandard conditions.7.2.1.3 The sealant manufac
24、turer may request conditionsother than those specified provided the temperature does notexceed 50C (122F).7.2.2 Remove the casting spacers from the specimens aftercuring.7.2.2.1 During the second week of the curing period, makeattempts to free the compound from the casting spacers at theends and bot
25、tom without damaging the sealant bead.7.2.2.2 Separate the casting spacers from the sealant as soonas practical during the curing period without damaging thesealant.7.3 Extend all specimens until the separation between thesubstrates provides the desired strain. Apply this strain at aminimum of 3 mm/
26、h (18 in./h).7.4 When the specimens have reached their specifiedextension, block the specimens with the appropriate separatorand remove from the extension device/machine. Do not re-move separators for the duration of test.7.5 Place three test specimens in water (minimum of 0.33 L(0.09 gal) per speci
27、men) at a specified temperature with thedefault being 23 6 2C. (73 6 4F). Ensure that the testspecimens are fully immersed.7.6 Leave three test specimens at standard conditions.7.7 Unless otherwise specified, record the length and widthof the adhesive and cohesive defects at 0, 24 and 168 h afterrea
28、ching the target strain at the standard conditions and waterimmersed conditions.7.8 Record adhesive and cohesive defects observed of eachof the test specimens. Record the number, location, length anddepth of the defect to the nearest 1 mm (132 in.) and note if theyare adhesive or cohesive for each s
29、ample. Photographs areadvisable so that a future review can be made.8. Test Report8.1 Report the following information:TABLE 1 Suggested Strains for a 12.7-mm (0.50-in.) Wide Sealant Joint.Sealant MovementRatingDistance between panelsat 1 movement ratingDistance between panelsat 1.5 movement ratingD
30、istance between panelsat 2 movement ratingDistance between panels at4 movement rating12.5 % 14.0 mm (0.55 in.) 14.7 mm (0.58 in.) 15.5 mm (0.61 in.) 19.0 mm (0.75 in.)25 % 15.5 mm (0.61 in.) 17.2 mm (0.68 in.) 19.0 mm (0.75 in.) 25.4 mm (1 in.)50 % 19.0 mm (0.75 in.) 21.8 mm (0.86 in.) 25.4 mm (1 in
31、.) 38.1 mm (1.5 in.)100 % 25.4 mm (1 in.) 31.8 mm (1.25 in.) 38.1 mm (1.5 in.) 63.5 mm (2.5 in.)C1635 1628.1.1 Sealant used, color, manufacturers lot number andrated movement capability per Specification C920 as desig-nated by the manufacturer,8.1.2 Actual dimensions of the joint and configuration,8
32、.1.3 Cleaning method,8.1.4 Description of the test substrate(s),8.1.5 Primer used,8.1.6 Curing method,8.1.7 Strain induced on the sealant during the test in % oforiginal joint width,8.1.8 Strain rate, and8.1.9 The immersion medium and temperature.8.1.10 Report the Nature of test effects observed, su
33、ch asamount of adhesive or cohesive failure, deformation, bubbles,or other characteristics, for each sample at 0, 24 and 168 h fordry and immersed samples.8.1.11 Deviations from standard conditions including sub-strates utilized, time of cure, use of primer, observations, andother deviations.9. Prec
34、ision and Bias9.1 Precision and bias testing involved two round-robintesting studies in five laboratories as noted below.39.1.1 The first study had five laboratories testing fivesealants.9.1.2 Results within a laboratory were repeatable within10 % and many of the results had no variation whatsoever.
35、 Ifthe sealant product adhered or did not adhere to the substrates,it did so consistently when fabricated by the same technician.9.1.3 Results from the first round robin showed that varia-tion between laboratories was up to 6100 %. However whenstudying the data carefully, it shows that two products
36、in thefive laboratories were the source of the variation. Three of thefive products showed variation between laboratories of 610 %.This result was encouraging.9.1.4 The second round-robin test was initiated between thesame five laboratories using the two products that gave thelarge deviations betwee
37、n laboratories. The leadership of thetest laboratories met in Kansas City, Missouri, United States, inJune of 2004 to discuss the variations of technique that canhappen in each laboratory. The group decided to retest the twoproducts that were the source of the large variation and focuson laboratory
38、technique.9.1.5 Results from the second study once again within asingle laboratory were repeatable within 10 % or less.9.1.6 Results between laboratories on one product testedwere repeatable within 10 % in all five laboratories. The otherproduct tested was repeatable within 10 % in four of fivelabor
39、atories and varied by 100 % in the fifth laboratory.10. Keywords10.1 adhesion; adhesive defect; casting spacer; cohesion;cohesive defect; constant strain; immersion; primer; sealant;separator; standard conditions; substrateASTM International takes no position respecting the validity of any patent ri
40、ghts asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at an
41、y time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments w
42、ill receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by A
43、STM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail);
44、or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ data have been filed at ASTM International Headquarters and maybe obtained by requesting Research Report RR:C24-1055.C1635 163