1、December 2015 English price group 14No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 83.080.01!%JwH“2398437www.din.d
2、eDIN EN ISO 22007-2Plastics Determination of thermal conductivity and thermal diffusivity Part 2: Transient plane heat source (hot disc) method (ISO 22007-2:2015);English version EN ISO 22007-2:2015,English translation of DIN EN ISO 22007-2:2015-12Kunststoffe Bestimmung der Wrmeleitfhigkeit und der
3、Temperaturleitfhigkeit Teil 2: Transientes Flchenquellenverfahren (Hot-Disk-Verfahren) (ISO 22007-2:2015);Englische Fassung EN ISO 22007-2:2015,Englische bersetzung von DIN EN ISO 22007-2:2015-12Plastiques Dtermination de la conductivit thermique et de la diffusivit thermique Partie 2: Mthode de la
4、source plane transitoire (disque chaud) (ISO 22007-2:2015);Version anglaise EN ISO 22007-2:2015,Traduction anglaise de DIN EN ISO 22007-2:2015-12SupersedesDIN EN ISO 22007-2:2012-04www.beuth.deDocument comprises 29 pagesDTranslation by DIN-Sprachendienst.In case of doubt, the German-language origina
5、l shall be considered authoritative.01.16 DIN EN ISO 22007-2:2015-12 2 A comma is used as the decimal marker. National foreword This document (EN ISO 22007-2:2015) has been prepared by Technical Committee ISO/TC 61 “Plastics” in collaboration with Technical Committee CEN/TC 249 “Plastics” (Secretari
6、at: NBN, Belgium). The responsible German body involved in its preparation was DIN-Normenausschuss Kunststoffe (DIN Standards Committee Plastics), Working Committee NA 054-01-03 AA Physikalische, rheologische und analytische Prfungen. The DIN Standard corresponding to the International Standard refe
7、rred to in this document is as follows: ISO 22007-1 DIN EN ISO 22007-1 Amendments This standard differs from DIN EN ISO 22007-2:2012-04 as follows: a) the values of thermal conductivity given in the scope have been changed; b) the sensitivity coefficient has been changed (3.3); c) the thickness rang
8、e for thin-film specimens has been changed (6.4); d) low thermally conducting specimens have been specified (8.5); e) precision and bias have been adapted (10.2); f) the Bibliography has been extended; g) normative references have been updated and the standard has been editorially revised. Previous
9、editions DIN EN ISO 22007-2: 2012-04 DIN EN ISO 22007-2:2015-12 3 National Annex NA (informative) Bibliography DIN EN ISO 22007-1, Plastics Determination of thermal conductivity and thermal diffusivity Part 1: General principles DIN EN ISO 22007-2:2015-12 4 This page is intentionally blank EUROPEAN
10、STANDARD NORME EUROPENNE EUROPISCHE NORM EN ISO 22007-2 August 2015 ICS 83.080.01 Supersedes EN ISO 22007-2:2012English Version Plastics - Determination of thermal conductivity and thermal diffusivity - Part 2: Transient plane heat source (hot disc) method (ISO 22007-2:2015) Plastiques - Dterminatio
11、n de la conductivit thermique et de la diffusivit thermique - Partie 2: Mthode de la source plane transitoire (disque chaud) (ISO 22007-2:2015) Kunststoffe - Bestimmung der Wrmeleitfhigkeit und der Temperaturleitfhigkeit - Teil 2: Transientes Flchenquellenverfahren (Hot-Disk-Verfahren) (ISO 22007-2:
12、2015) This European Standard was approved by CEN on 20 June 2015. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical
13、references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of
14、a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Mace
15、donia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUR
16、OPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2015 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN ISO 22007-2:2015 Eworldwide for CEN national Members. Foreword Introduction .1 Scope .2 Normative references 3 Terms and
17、definitions .4 Principle 5 Apparatus .6 Test specimens.6.1 Bulk specimens 6.2 Anisotropic bulk specimens .6.3 Slab specimens .6.4 Thin-film specimens 7 Procedure8 Calculation of thermal properties .8.1 Bulk specimens 8.2 Anisotropic bulk specimens . 178.3 Slab specimens . 188.4 Thin-film specimens 1
18、98.5 Low thermally conducting specimens .8.5.1 Introductory remarks .8.5.2 Low thermally conducting bulk specimens .8.5.3 Low thermally conducting anisotropic bulk specimens .8.5.4 Low thermally conducting thinfilm specimen 9 Calibration and verification .9.1 Calibration of apparatus 9.2 Verificatio
19、n of apparatus .10 Precision and bias 11 Test report Bibliography .2Contents Page2European foreword 3EN ISO 22007-2:2015 (E) 45666881010111112121414202020222222232324522.DIN EN ISO 22007-2:2015-12 3 European foreword This document (EN ISO 22007-2:2015) has been prepared by Technical Committee ISO/TC
20、 61 “Plastics” in collaboration with Technical Committee CEN/TC 249 “Plastics” the secretariat of which is held by NBN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by February 2016, and conflicti
21、ng national standards shall be withdrawn at the latest by February 2016. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document
22、 supersedes EN ISO 22007-2:2012. According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav R
23、epublic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. Endorsement notice The text of ISO 22007-2:2015 has be
24、en approved by CEN as EN ISO 22007-2:2015 without any modification. EN ISO 22007-2:2015 (E) DIN EN ISO 22007-2:2015-12 ForewordISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Stan
25、dards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also t
26、ake part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.The procedures used to develop this document and those intended for its further maintenance are described in the ISO/IEC Directives, Part 1. In p
27、articular the different approval criteria needed for the different types of ISO documents should be noted. This document was drafted in accordance with the editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives). Attention is drawn to the possibility that some of the elements
28、of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of any patent rights identified during the development of the document will be in the Introduction and/or on the ISO list of patent declarations received (se
29、e www.iso.org/patents). Any trade name used in this document is information given for the convenience of users and does not constitute an endorsement.For an explanation on the meaning of ISO specific terms and expressions related to conformity assessment, as well as information about ISOs adherence
30、to the WTO principles in the Technical Barriers to Trade (TBT) see the following URL: Foreword - Supplementary informationThe committee responsible for this document is ISO/TC 61, Plastics, Subcommittee SC 5, Physical-chemical properties.This second edition cancels and replaces the first edition (IS
31、O 22007-2:2008), which has been technically revised.The main changes are the following:a) Values of thermal conductivity in scope revised;b) Sensitivity coefficient revised (3.3);c) Thickness range for thin-film specimens changed (6.4);d) Low thermally conducting specimens specified (8.5);e) Precisi
32、on and bias adapted; (10.2);f) Bibliography extended;g) Normative references updated and standard editorial revised.ISO 22007 consists of the following parts, under the general title Plastics Determination of thermal conductivity and thermal diffusivity: Part 1: General principles Part 2: Transient
33、plane heat source (hot disc) method Part 3: Temperature wave analysis method Part 4: Laser flash method Part 5: Results of interlaboratory testing of poly(methyl methacrylate) samples Technical Report Part 6: Comparative method for low thermal conductivities using a temperature-modulation technique4
34、EN ISO 22007-2:2015 (E) DIN EN ISO 22007-2:2015-12 IntroductionA significant increase in the development and application of new and improved materials for broad ranges of physical, chemical, biological, and medical applications has necessitated better performance data from methods of measurement of
35、thermal-transport properties. The introduction of alternative methods that are relatively simple, fast, and of good precision would be of great benefit to the scientific and engineering communities. 1A number of measurement techniques described as transient methods have been developed and several ha
36、ve been commercialized. These are being widely used and are suitable for testing many types of material. In some cases, they can be used to measure several properties separately or simultaneously. 2,3A further advantage of some of these methods is that it has become possible to measure the true bulk
37、 properties of a material. This feature stems from the possibility of eliminating the influence of the thermal contact resistance (see 8.1.1) that is present at the interface between the probe and the specimen surfaces. 1,3,4,5,65EN ISO 22007-2:2015 (E) DIN EN ISO 22007-2:2015-12 1 ScopeThis part of
38、 ISO 22007 specifies a method for the determination of the thermal conductivity and thermal diffusivity, and hence the specific heat capacity per unit volume of plastics. The experimental arrangement can be designed to match different specimen sizes. Measurements can be made in gaseous and vacuum en
39、vironments at a range of temperatures and pressures.This method is suitable for testing homogeneous and isotropic materials, as well as anisotropic materials with a uniaxial structure. The homogeneity of the material extends throughout the specimen and no thermal barriers (except those next to the p
40、robe) are present within a range defined by the probing depth(s) (see 3.2 below).The method is suitable for materials having values of thermal conductivity, , in the approximate range 0,010 Wm1K1 500 Wm1K1, values of thermal diffusivity, , in the range 5 108m2s1 104m2s1, and for temperatures, T, in
41、the approximate range 50 K T 1 000 K.NOTE 1 The specific heat capacity per unit volume, C, can be obtained by dividing the thermal conductivity, , by the thermal diffusivity, , i.e. C = /, and is in the approximate range 0,005 MJm3K1 C 5 MJm3K1. It is also referred to as the volumetric heat capacity
42、.NOTE 2 If the intention is to determine the thermal resistance or the apparent thermal conductivity in the through-thickness direction of an inhomogeneous product (for instance a fabricated panel) or an inhomogeneous slab of a material, reference is made to ISO 8301, ISO 8302, and ISO 472.The therm
43、al-transport properties of liquids can also be determined, provided care is taken to minimize thermal convection.2 Normative referencesThe following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the c
44、ited edition applies. For undated references, the latest edition of the referenced document (including any amendments) applies.ISO 22007-1, Plastics Determination of thermal conductivity and thermal diffusivity Part 1: General principles3 Terms and definitionsFor the purposes of this document, the t
45、erms and definitions given in ISO 22007-1 and the following apply.3.1penetration depthppenmeasure of how far into the specimen, in the direction of heat flow, a heat wave has travelledNote 1 to entry: For this method, the penetration depth is given by6EN ISO 22007-2:2015 (E) DIN EN ISO 22007-2:2015-
46、12 ptpentot=wherettotis the total measurement time for the transient recording; is the thermal diffusivity of the specimen material; is a constant dependent on the sensitivity of the temperature recordings.Note 2 to entry: It is expressed in metres (m).3.2probing depthpprobmeasure of how far into th
47、e specimen, in the direction of heat flow, a heat wave has travelled during the time window used for calculationNote 1 to entry: The probing depth is given byptprob=maxwheretmaxis the maximum time of the time window used for calculating the thermal-transport proper-ties.Note 2 to entry: It is expres
48、sed in metres (m).Note 3 to entry: A typical value in hot disc measurements is = 2, which is assumed throughout this part of ISO 22007.3.3sensitivity coefficientqcoefficient defined by the formulaqqTtq=()whereq is the thermal conductivity, , the thermal diffusivity, , or the volumetric specific heat
49、 capacity, C;T(t) is the mean temperature increase of the probe.Note 1 to entry: Different sensitivity coefficients are defined for thermal conductivity, thermal diffusivity, and specific heat per unit volume.7Note 2 to entry: To define the time window that is used to determine both the thermal conductivity and diffusivity from one single experiment, the theory of sensitivity co