1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 10 20 N-STATUS Replaced by WSS-M13P13-A L. Schmalz, FNA 2004 02 09 Activated G Barr Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 2 GREASE, NLGI GRADE 3, ANTI-ROLL BAR WSS-M1C269-A NOT TO BE USED
2、FOR NEW DESIGN 1. SCOPE This specification defines the physical properties of a lubricating paste consisting of an inorganic soap, white solid lubricants and a Polyalphaolefin (PAO) synthetic mineral oil. 2. APPLICATION This specification was originally released for use to aid bush and clamp assembl
3、y on anti-roll bars. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.1 The supplier must furnish to the affected Materials Engineering activity a
4、 completed and certified copy of the attached Supplement A. Test methods stated for guidance only and other applicable methods may be accepted. Only tests applicable to the intended application as agreed between the supplier and the affected Materials Engineering activity are required. 3.2 COLOR Whi
5、te 3.3 FORM Paste 3.4 ODOR Materials shall produce no objectionable odour during testing herein 3.5 FLASH POINT, C, min 285 (ASTM D 92) 3.6 DENSITY (20 C) 1.048 (DIN 51757) g/cm33.7 FLOW PRESSURE (DIN 51805) 3.7.1 20 C, 180 +/- 10% 3.7.2 - 20 C 320 +/- 10% 3.7.3 - 35 C 495 +/- 10% ENGINEERING MATERI
6、AL SPECIFICATIONWSS-M1C269-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 2 3.8 PENETRATION (DIN ISO 2137) Worked, 60 strokes (mm/10) 220 - 250 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the re
7、quirements of this specification. 4.1 Test Methods The test methods shown are for indication only if the methods shown are impracticable then alternative methods may be accepted. The use of alternative methods should be confirmed by the responsible Materials Engineering activity before the submission of any data.