1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 01 06 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, SHORE PATTERN, WARP KNIT WSS-M1H1020-A 1. SCOPE The material defined by this specification is a SHORE embossed
2、 pattern, 4 bars, 56 Gauge, Single Needle bar, body cloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for 2008 U377 MERCURY MARINER seat insert. 3. REQUIREMENTS In addition, to the requirements listed
3、 herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabri
4、c Count, +/- 5% tolerance (ASTM D 3887) Wales 154 wales/10 cm Courses 240 courses/10 cm 3.2.2 Fabric Weight, +/- 5%, g/m2(FLTM BN 106-01) Face w/ no Backcoat 342 Laminated to 3 mm foam 475 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Polyester Backcoat No backco
5、at ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1020-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 10% 11.1 tex f34 (textured yarn) Middle 10% 11.1 texf34 (textured yarn) Back 56% 11.1 tex f100 (textured yarn) 4th24% 7.8 texf34 (textured yarn) 3.5 METHOD OF DYEING Piece Dye 3.6 FINISHING OPERATIONS Knit, Heat set, Setmake, Dye, Tenter dry, Emboss, Inspect