1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2008 11 26 N-STATUS No Replacement L. Schmalz, FNA / M. Montgomery, FOE2003 03 19 Revised Para 3.0 inserted ; Para 3.1, 3.2, 3.3, 3.15, 3.16, 4 deleted 1996 07 22 Activated N. J. Komatsu Printed copies are u
2、ncontrolled Page 1 of 4 Copyright 2008, Ford Global Technologies, Inc. FABRIC, MATCH PATTERN, WOVEN JACQUARD, UNLAMINATED WSS-M1H714-A FABRIC, MATCH PATTERN, WOVEN JACQUARD, 3mm WSS-M1H714-B1 FABRIC, MATCH PATTERN, WOVEN JACQUARD, 6mm WSS-M1H714-B2 FABRIC, MATCH PATTERN, WOVEN JACQUARD, 3mm WSS-M1H7
3、14-C1 FABRIC, MATCH PATTERN, WOVEN JACQUARD, 6mm WSS-M1H714-C2 FABRIC, MATCH PATTERN, WOVEN JACQUARD, 6mm WSS-M1H714-D2 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by these specifications is a woven jacquard polyester face fabric which can be flame laminated to polyester or polyether
4、 urethane foam and backed with a knitted fabric. It can also be backed with an HFW weldable backcoating. 2. APPLICATION WSS-M1H714-A is used for molded headrests and also adhesive coated for use on inner door panels. WSS-M1H714-B1, B2, C1, C2, are for seat wearing surfaces. WSS-M1H714-D2 is used for
5、 adhesively bonded door and quarter trim panel applications. WSS-M1H714-A Unlaminated WSS-M1H714-B1 3.0 mm, flame laminated to polyether foam and knitted fabric WSS-M1H714-B2 6.0 mm, flame laminated to polyether foam and knitted fabric WSS-M1H714-C1 3.0 mm, flame laminated to polyester foam and knit
6、ted fabric (EAO use only) WSS-M1H714-C2 6.0 mm, flame laminated to polyester foam and knitted fabric (EAO use only) WSS-M1H714-D2 6.0 mm, flame laminated to polyether foam 3. REQUIREMENTS In addition to the requirements listed herein, the fabric or laminate shall meet all requirements of WSB-M8P1-I.
7、 ENGINEERING MATERIAL SPECIFICATION WSS-M1H714-A/B1/B2/C1/C2/D2 Page 2 of 4 Copyright 2008, Ford Global Technologies, Inc. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P111
8、1-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 5 % tolerance (ASTM D 3775) Warp 280 ends/10 cm Weft 220 picks/10cm 3.4.2 Fabric Weight, range 330 - 380 g/m2(FLTM BN 106-01) 3.5 COMPOSITION (ASTM D 629) 100 % Polyester 3.6 YARN CONSTRUCTION (ASTM D 1244) Warp 540 dtex, f144 (polyester, semi-du
9、l air texturised) Weft 850 dtex, f192 (polyester, bright, air texturised) 3.7 METHOD OF DYING Yarn dyed or as approved by Material Engineering 3.8 FINISHED OPERATIONS As approved by Material Engineering 3.9 REQUIREMENTS FOR POLYESTER FOAM As specified in WSD-M2D243-A4 3.10 REQUIREMENTS FOR POLYETHER
10、 FOAM As specified in WSD-M2D243-A2 3.11 REQUIREMENTS FOR THE As pecifed inBACKING FABRIC (B1, B2) WSD-M9H111-B ENGINEERING MATERIAL SPECIFICATION WSS-M1H714-A/B1/B2/C1/C2/D2 Page 3 of 4 Copyright 2008, Ford Global Technologies, Inc. 3.12 REQUIREMENTS FOR BACKING As specified in FABIC (1, C2) WSD-M9
11、H136-A 3.13 REQUIREMENTS FOR THE FLAME LAMINATED MATERIAL 3.13.1 Thickness, range (ASTM D 1777, circular presser foot area 645 mm2, 2.8 g force, 43 Pa pressure) WSS-M1H714-B1 3.0 +/- 0.5 mm WSS-M1H714-B2 6.0 +/- 0.5 mmWSS-M1H714-C1 3.0 +/- 0.5 mm WSS-M1H714-C2 6.0 +/- 0.5 mmWSS-M1H714-D2 6.0 +/- 0.5
12、 mm 3.13.2 Compressed Thickness (ASTM D 1777, circular presser foot area 645 mm2, 1 kg force, 5 s dwell) WSS-M1H714-D2 2.45 +/- 0.3 mm 3.13.3 Weight, range (FLTM BN 106-01) WSS-M1H714-B1 510 +/- 40 g/m2WSS-M1H714-B2 620 +/- 40 g/m2WSS-M1H714-C1 510 +/- 40 g/m2WSS-M1H714-C2 620 +/- 40 g/m2WSS-M1H714-
13、D2 620 +/- 40 g/m23.13.4 Stretch and Set, range (SAE J855) Stretch (B1, B2, C1, C2) Warp 1 - 10 % Weft 1 -10Set (B1, B2, C1, C2) Warp 0 - 5 % Weft 0 -53.13.5 Modulas, max (WSS-M1H714-D2) Strain, 6 % Warp 180 N Weft 280 N ENGINEERING MATERIAL SPECIFICATION WSS-M1H714-A/B1/B2/C1/C2/D2 Page 4 of 4 Copy
14、right 2008, Ford Global Technologies, Inc. 3.14 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute Note: Not required on face fabric when used as a fully bonded composite. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of these specifications. 5.1 Purchase departments will ensure that both materials defined in these specifications and shipped to any one assembly plant will be produced by one supplier only.