FORD WSS-M2D489-A1-2009 SILICONE (VMQ) RUBBER IMPROVED COMPRESSION SET 60 DUROMETER LOW VOLATILES LONG LIFE GASKET TO BE USED WITH FORD WSS-M99P1111-A 《长寿命垫片用低挥发物含量的硬度为60的高压缩永久变形.pdf

上传人:fatcommittee260 文档编号:752831 上传时间:2019-01-14 格式:PDF 页数:3 大小:27.35KB
下载 相关 举报
FORD WSS-M2D489-A1-2009 SILICONE (VMQ) RUBBER IMPROVED COMPRESSION SET 60 DUROMETER LOW VOLATILES LONG LIFE GASKET  TO BE USED WITH FORD WSS-M99P1111-A  《长寿命垫片用低挥发物含量的硬度为60的高压缩永久变形.pdf_第1页
第1页 / 共3页
FORD WSS-M2D489-A1-2009 SILICONE (VMQ) RUBBER IMPROVED COMPRESSION SET 60 DUROMETER LOW VOLATILES LONG LIFE GASKET  TO BE USED WITH FORD WSS-M99P1111-A  《长寿命垫片用低挥发物含量的硬度为60的高压缩永久变形.pdf_第2页
第2页 / 共3页
FORD WSS-M2D489-A1-2009 SILICONE (VMQ) RUBBER IMPROVED COMPRESSION SET 60 DUROMETER LOW VOLATILES LONG LIFE GASKET  TO BE USED WITH FORD WSS-M99P1111-A  《长寿命垫片用低挥发物含量的硬度为60的高压缩永久变形.pdf_第3页
第3页 / 共3页
亲,该文档总共3页,全部预览完了,如果喜欢就下载吧!
资源描述

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 09 22 N-STATUS Use industry standard C. Mracna, NA 2004 10 20 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.3, 3.9, 3.10 & 4 1995 06 30 Activated E. J. Duda Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 1

2、of 3 SILICONE (VMQ) RUBBER, IMPROVED COMPRESSION WSS-M2D489-A1 SET, 60 DUROMETER, LOW VOLATILES, LONG LIFE GASKET NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a medium modulus, silicone rubber with low silicone volatiles, good compression set and stress relaxa

3、tion, suitable for high temperature service conditions. 2. APPLICATION This specification was released originally for material used as the third generation best-in-class gasket where moderate to high compressive strength at moderate to high temperature is required for use as cam cover, oil pan and f

4、ront cover gaskets. Low volatile silicone rubber is needed to prevent silica contamination of emission components. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS

5、-M99P1111-A). 3.4 MATERIAL TESTING 3.4.1 Preparation of Test Specimens Test specimens may be taken from either test sheets or molded parts. To insure a proper cutting of specimens, backup all test sheets/parts with cardboard or a rubber sheet. The test sheets shall have the following dimensions: 150

6、 x 150 mm, min x 2.0 +/- 0.2 mm. . Tensile Strength per ISO 37/ASTM D 412, die C, full thickness. If the length between the compression limiters is not long enough to accommodate a die C, use a die exactly one-half the dimensions of the die C. . Tear Strength per ISO 34/ASTM D 624, full thickness. .

7、 Volume Change - 25 mm x part width x part thickness. . Compression Set - 25 mm long x part width x single thickness minus any skirt. Do not buff any sample including those with a bead, except for compression set. 3.5 ORIGINAL PROPERTIES 3.5.1 Density 1.18 - 1.23 g/cm3(ISO 1183, Method A/ASTM D 297)

8、 ENGINEERING MATERIAL SPECIFICATIONWSS-M2D489-A1Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 2 of 3 3.5.2 Hardness, International 55 - 67 (ISO 48/ASTM D 1415) 3.5.3 Hardness, Durometer A 55 - 67 (ISO 868/ASTM D 2240, instantaneous, plied-up specimen. Hand held d

9、urometers shall not be used) 3.5.4 Tensile Strength, min 5.8 MPa (ISO 37/ASTM D 412, Die C) 3.5.5 Elongation at Break, min 210% (Test Method according to para 3.5.4) 3.5.6 Modulus at 100% Elongation 2100 - 3000 kPa (Test Method according to para 3.5.4) 3.5.7 Tear Strength, min 12 kN/m (ISO 34, Metho

10、d C/ASTM D 624, Die B) 3.5.8 Low Temperature Retraction -45 C (RT-10)(ASTM D 1329) 3.5.9 Ozone Resistance, max Rating 0 (FLTM BP 101-01, Procedure A) 3.5.10 Compression Set, max 28% (ISO 815/ASTM D 395, Method B, except 25% compression, plied-up specimens) 3.5.10.1 22 h at 175 +/- 2 C 3.5.11 Silicon

11、e Volatiles, as received at Ford, max 0.60% (FLTM AV 102-01) 3.5.12 Compression Stress Relaxation (ISO 3384/ASTM TBD) Washer sampler # 3, 25% compression 1000 h, 150 +/- 2 C in IRM 903 Force Retention, min 20% 3.6 HEAT AGED (ISO 188/ASTM D 573, 150 +/- 50 air changes/h, 1000 h at 150 +/- 2 C) 3.6.1

12、Hardness Durometer A Change, max +10 3.6.2 Tensile Strength Change, max -18% 3.6.3 Elongation Change, max -38% 3.6.4 Visual Evaluation No surface tackiness or cracks when folded flat against itself. ENGINEERING MATERIAL SPECIFICATIONWSS-M2D489-A1Printed copies are uncontrolled Copyright 2009, Ford G

13、lobal Technologies, LLC Page 3 of 3 3.7 IMMERSION IN OIL IRM 902 (ISO 1817/ASTM D 471, 1000 h at 150 +/- 2 C) 3.7.1 Hardness Durometer A Change, max -16 3.7.2 Tensile Strength Change, max -20% 3.7.3 Elongation Change, max -22% 3.7.4 Volume Change +11% 3.7.5 Visual Evaluation No surface tackiness or cracks when folded flat against itself. 3.8 COMPRESSION MODULUS 1300 - 2100 kPa (ASTM D 575, Method A, 25% deflection) 5. GENERAL INFORMATION The information below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 RECYCLING CODE VMQ