1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2004 01 29 Revised Para 3.0 inserted; paras 3.1, 3.11, 4 deleted 1989 01 04 Released NE01E10000474035Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 1 of 2 LUBRICANT, SYNTHETIC POLYOL ESTER ESE-M99C115-A 1. S
2、COPE This material specification defines the minimum acceptable performance requirements and physical/chemical properties of a polyol ester based synthetic fluid with good oxidation stability. 2. APPLICATION This specification was released originally for material used to lubricate supercharger assem
3、blies. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 VISCOSITY at 100 C8.6 - 9.6 mm2/s (ASTM D 445 or ISO 3104) 3.3 VISCOSITY at -35 C, max25,0
4、00 mm2/s (ASTM D 445 or ISO 3104) 3.4 DENSITY at 25 C, min0.90 (ASTM D 1217) 3.5 FLASH POINT, min 260 C (ASTM D 92 or ISO 2592) 3.6 POUR POINT, max -40 C (ASTM D 97 or ISO 3016) 3.7 EVAPORATION LOSS, max 1% (ASTM D 972, 24 h at 100 C) 3.8 TOTAL ACID NUMBER, max 1 mg KOH/g (ASTM D 974) ENGINEERING MA
5、TERIAL SPECIFICATIONESE-M99C115-APrinted copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 2 of 2 3.9 CORROSIVENESS AND OXIDATION STABILITY (FTM 791b, Method 5308, 72 h at 175 C) Change in Viscosity at 40 C (ASTM D 445), max 10% Change in Neutralization Number, max 1 mg KOH/g Evaporation Loss, max 2% Change in Weight of Metals, mg/cm2, max Aluminum 0.6 Brass 0.6 Bronze 0.6 Copper 0.6 Nickel 0.2 Steel 0.2 3.10 WEAR PREVENTIVE CHARACTERISTICS, FOUR-BALL METHOD (ASTM D 2266, 600 rpm and 25 C) Wear Scar Diameter, max 1 mm