1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2007 08 31 Activated M.Dumitrescu Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC Page 1 of 2 FABRIC, ECO RF- USA PATTERN, FLAT WOVEN 100% POST WSS-M1H1023-A2 INDUSTRIAL TREATED WITH REPELLANT FINISH 1. SCOPE The
2、material defined by this specification is an ECO RF USA pattern, Dobby flat woven bodycloth of good quality and uniform composition. The fabric is made of 100% Post-Industrial yarn. The fabric is treated with a repellant finish (RF) to prevent staining. 2. APPLICATION This specification was released
3、 originally for material used as an interior trim fabric for the 2007 1/2 U377 Escape Hybrid, seat bolster. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of: WSS-M8P18-A1/A4, as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Mat
4、erial suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3775) Warp 355 ends/10 cm Fill 245 picks/10 cm 3.2.2 Fabric Weight, +/- 5% tolerance (FLTM BN 106-01)
5、Face Fabric w/ backcoat 411 g/m2Laminated to 3mm foam 525 g/m2 3.5 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4. Fabric 100% Post- Industrial Polyester Backcoating Acrylic Latex ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1023-A2 Printed copies are uncontrolled Copyright 2007, For
6、d Global Technologies, LLC Page 2 of 2 3.6 YARN CONSTRUCTION (ASTM D 1244) Warp A. 16.7 tex f34 (false twist post industrial polyester yarn) x 2 polyester) x 3 Fill W 16.7 tex f34 (false twist post industrial polyester yarn) x 2 X 33.3 tex f72 (false twist post industrial polyester yarn) x 2 3.7 METHOD OF DYEING Piece Dyed 3.8 FINISHING OPERATIONS Dye, RF treatment, Dry, Backcoat, Dry Note: Eco RF - USA fabric is treated with maximum 1% repellant finish (RF) to prevent staining caused by water based agents.