1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 03 19 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 2 FABRIC, AUSTIN II PATTERN, FLAT WOVEN WSS-M1H1131-A 1. SCOPE The material defined by this specification is a Austin II
2、 pattern, flat woven bodycloth of good quality and uniform composition. The fabric is backcoated. 2. APPLICATION This specification was released originally for material used as a seat fabric, insert application for 2009 P415. 3. REQUIREMENTS Material specification requirements are to be used for ini
3、tial qualification of materials. In addition to the requirements listed herein, the fabric shall meet all requirements of: WSS-M8P18-A1/A4. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Mater
4、ials (WSS-M99P1111-A) 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3775) Warp 340 ends/10 cm Fill 189 picks/10 cm 3.2.2 Fabric Weight, +/- 5% tolerance (FLTM BN 106-01) Face Fabric w/backcoat 391 g/m23.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4. Fabr
5、ic 100% Polyester Backcoating Latex ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1131-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 16.7 tex f34 (textured semi-dull polyester) x 3 Fill 16.7 tex f34 (textured, semi-dull polyester, sol dye) x 3 3.5 METHOD OF DYEING piece dye/solution dye 3.6 FINISHING OPERATIONS woven, wash, dye, backcoated