1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions Rev. 0 2009 05 28 Activated M. Dumitrescu, NA Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 1 of 2 FABRIC, TRIBECA PATTERN, WARP KNIT WSS-M1H1211-A 1. SCOPE The material defined by this specification is a T
2、RIBECA PATTERN, 4 bars, 28 Gauge, warp knit, body cloth of good quality and uniform composition. The fabric is approved as a tri-laminated fabric 2. APPLICATION This specification was released originally for material used as an interior trim fabric for U387 2011 seat bolster/insert. 3. REQUIREMENTS
3、In addition, to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-
4、A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 120 wales/10 cm Courses 170 courses/10 cm 3.2.2 Fabric Weight, +/- 5%, g/m2 (FLTM BN 106-01) Face fabric w/no Backcoat 330 Backing scrim 45 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabr
5、ic 100% Polyester Backing scrim Warp Knit Polyester Scrim ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1211-A Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 7.8 tex f36 (semi-dull, textured yarn) Middle 15 tex f48 (semi-
6、dull, textured yarn) Back 4.5 tex f24 (semi-dull, flat yarn) 4th 7.8 tex f36 (semi-dull, textured yarn) 3.5 METHOD OF DYEING Solution dye 3.6 FINISHING OPERATIONS Wash, preset, heatset, inspect 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase department will ensure that the material defined in this specification and shipped to any one assembly plant will be produced by one supplier only.