1、A.C.N. 006 893 232Holden LimitedEngineering DepartmentMATERIAL SPECIFICATIONNUMBERSHEETRELEASEREVISION:HN 22461 of 3September, 1998NAME: TAPE - CONFORMABLETHIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TOTHE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TOCONFIRM THE DOCUMENT ISSUE DATE
2、IS STILL VALID.FORM : I:LABRTORYFORMSTDMATSPEC.DOC1. SCOPEThis specification describes the physical and performance properties of a non-woven sound abatement tape. The tape consists of a non-woven material coatedon one side with a pressure sensitive adhesive protected by a silicon releasepaper.The t
3、ape is used for sound abatement applications where two dissimilar surfacescome into contact causing a rubbing or squeaking noise.2. REFERENCESHN1000 ASTM D1000 ASTM D1004SAE J369 SAE J13513. PROPERTESMaterial Requirement3.1 Colour Black3.2 180 Mean Peel Strength(Refer ASTM D1000)ABS 650 N/m min.Poly
4、propylene 280 N/m min.3.3 Aged Adhesion72 hours at 70C, after ABS 825 N/m min.24 hours at 38C, 95% R.H. Polypropylene 235 N/m min.A.C.N. 006 893 232Holden LimitedEngineering DepartmentMATERIAL SPECIFICATIONNUMBERSHEETRELEASEREVISION:HN 22462 of 3September, 1998NAME: TAPE - CONFORMABLETHIS DOCUMENT M
5、UST NOT BE REPRODUCED. IF USED IN RELATION TOTHE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TOCONFIRM THE DOCUMENT ISSUE DATE IS STILL VALID.FORM : I:LABRTORYFORMSTDMATSPEC.DOC3. PROPERTIES (continued)Material Requirement3.4 Shear Strength(Refer ASTM D1000)Cold tested at -18C, after ABS 0.15 MPa
6、 min.24 hours at -18C Polypropylene 0.15 MPa minHot tested at 60C, after 24 ABS 0.20 MPa min.hours at 60C Polypropylene 0.20 MPa min3.5 Tear Resistance 15 N min.(Refer ASTM D1004)3.6 Elongation at Break 300% min(Refer ASTM D1000)3.7 Abrasion ResistanceTaber Abrasion CS10 wheels Dry 500 g - 1500 cycl
7、es minNumber of cycles to fail Wet 250g - 1000 cycles min.3.8 Humidity Resistance48 hours at 38C and 95%R.H.No visible loss of adhesion between tapeand substrate.3.9 Heat Resistance30 minutes at120CNo visible loss ofadhesion betweentape & substrate.168 hours at 82C No visible lossof adhesionbetween
8、tape &substrate.A.C.N. 006 893 232Holden LimitedEngineering DepartmentMATERIAL SPECIFICATIONNUMBERSHEETRELEASEREVISION:HN 22463 of 3September, 1998NAME: TAPE - CONFORMABLETHIS DOCUMENT MUST NOT BE REPRODUCED. IF USED IN RELATION TOTHE COMPANYS PRODUCTS THE RECIPIENT IS RESPONSIBLE TOCONFIRM THE DOCU
9、MENT ISSUE DATE IS STILL VALID.FORM : I:LABRTORYFORMSTDMATSPEC.DOC3. PROPERTIES (continued)Material Requirement3.10 Flammability, Burn Rate 100 mm/minute(Refer SAE J369) max.3.11 Odour Dry - Rating 2 max.(Refer SAE J1351) Wet Rating 3 max.3.12 Shelf Life Material shall pass all requirement of thissp
10、ecification after 90 days at 35C3.13 Construction Total Thickness 0.42 mmMaterial Type PolyurethaneConstruction Non-wovenPressure Sensitive Acrylic Adhesive4. APPROVAL, INSPECTION AND REJECTIONRefer HN 1000, Clauses C and G.5. HAZARDOUS MATERIALSRefer HN 1000, Clause H6. RESTRICTED CHEMICALSRefer HN 1000, Clause J7. APPROVED SUPPLIERS AND MATERIALSAPPROVED SUPPLIER APPROVED MATERIAL3M Conformable Tape 9343Prepared by: Ron Boyack