1、 ISO 2012 Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles Part 5: Round, square and hexagonal bars Tolerances on shape and dimensions Aluminium et alliages daluminium corroys Barres, tubes et profils fils Partie 5: Barres rondes, carres et hexagonales Tolrances sur form
2、e et dimensions INTERNATIONAL STANDARD ISO 6362-5 Third edition 2012-07-01 Reference number ISO 6362-5:2012(E) ISO 6362-5:2012(E) ii ISO 2012 All rights reserved COPYRIGHT PROTECTED DOCUMENT ISO 2012 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or ut
3、ilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fa
4、x + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ISO 6362-5:2012(E) ISO 2012 All rights reserved iii Contents Page Foreword iv 1 Scope 1 2 Normative references . 1 3 Terms and definitions . 1 4 Materials . 1 5 Tolerances on dimensions 2 5.1 Tolerances on diameter
5、and width across flats 2 5.2 Circularity of round bars . 2 5.3 Corner radii of square and hexagonal bars . 2 5.4 Fixed-length tolerances . 3 5.5 Squareness of cut ends . 3 6 Tolerances on shape 3 6.1 General . 3 6.2 Straightness tolerances . 3 6.3 Convexity/concavity . 4 6.4 Twist tolerances . 4 6.5
6、 Squareness for square bars . 5 ISO 6362-5:2012(E) Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Eac
7、h member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the Internation
8、al Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standard
9、s adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject o
10、f patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 6362-5 was prepared by Technical Committee ISO/TC 79, Light metals and their alloys, Subcommittee SC 6, Wrought aluminium and aluminium alloys. This third edition cancels and replaces the second edi
11、tion (ISO 6362-5:2001), which has been technically revised. ISO 6362 consists of the following parts, under the general title Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles : Part 1: Technical conditions for inspection and delivery Part 2: Mechanical properties Part 3:
12、 Extruded rectangular bars Tolerances on shape and dimensions Part 4: Profiles Tolerances on shape and dimensions Part 5: Round, square and hexagonal bars Tolerances on shape and dimensions Part 6: Round, square, rectangular and hexagonal tubes Tolerances on shape and dimensions Part 7: Chemical com
13、position iv ISO 2012 All rights reserved INTERNATIONAL STANDARD ISO 6362-5:2012(E) Wrought aluminium and aluminium alloys Extruded rods/ bars, tubes and profiles Part 5: Round, square and hexagonal bars Tolerances on shape and dimensions 1 Scope This part of ISO 6362 specifies the tolerances on dime
14、nsions and shape of the following: wrought aluminium and aluminium alloy extruded round bars, having diameters in the range from 8 mm up to 350 mm; wrought aluminium and aluminium alloy extruded square and hexagonal bars, having widths across flats in the range from 10 mm up to 220 mm. It applies to
15、 extruded round, square and hexagonal bars. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any ame
16、ndments) applies. ISO 6362-1, Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles Part 1: Technical conditions for inspection and delivery 3 Terms and definitions For the purposes of this document, the terms and definitions given in ISO 6362-1 apply. 4 Materials For the pur
17、poses of this part of ISO 6362, wrought aluminium and aluminium alloys are divided into two groups, which correspond to varying difficulty when manufacturing the products. The division into group I and group II of the most commonly used general engineering alloys is specified in Table 1. Grouping of
18、 other alloys is subject to agreement between the purchaser and supplier. ISO 2012 All rights reserved 1 ISO 6362-5:2012(E) Table 1 Alloy group Group I 1070, 1070A, 1060, 1050, 1050A, 1350, 1100, 1200 3102, 3003, 3103 5005, 5005A, 5051A, 5251 6101, 6101A, 6101B, 6005, 6005A, 6005C, 6110A, 6012, 6018
19、 6023, 6351, 6060, 6360, 6061, 6261, 6262, 6262A, 6063, 6063A, 6463, 6065, 6081, 6082,6182 Group II 2007, 2011, 2011A, 2014, 2014A, 2017, 2017A, 2024, 2030 5019, 5049, 5052, 5154A, 5454, 5754, 5056, 5083, 5086 7003, 7204, 7005, 7108, 7108A, 7020, 7021, 7022, 7049A, 7050, 7075 NOTE The four-digit nu
20、mbers listed are taken from the Registration of International Alloy Designations and Chemical Composition Limits for Wrought Aluminium Alloys, published by the Aluminum Association, 1525 Wilson Boulevard, Suite 600, Arlington, VA 22209, USA (known as “Teal Sheets”). 5 Tolerances on dimensions 5.1 To
21、lerances on diameter and width across flats Tolerances on diameter and width across flats shall be in accordance with Table 2. Table 2 Dimensional tolerances Dimensions in millimetres Diameter or width across flats b Tolerances Alloy group I Alloy group II 8 b 18 0,22 0,30 18 b 25 0,25 0,35 25 b 40
22、0,30 0,40 40 b 50 0,35 0,45 50 b 65 0,40 0,50 65 b 80 0,50 0,70 80 b 100 0,55 0,90 100 b 120 0,65 1,00 120 b 150 0,80 1,20 150 b 180 1,00 1,40 180 b 220 1,15 1,70 220 b 270 1,30 2,00 270 b 320 1,60 2,50 320 b 350 2,10 3,00 When the tolerance is specified as either all plus or minus side, the value i
23、n this table shall be doubled. 5.2 Circularity of round bars Circularity is measured by the difference between the maximum and minimum diameters measured in the same cross-section. The permissible circularity is included in the tolerances on diameter specified in Table 2. 5.3 Corner radii of square
24、and hexagonal bars The maximum corner radii of square and hexagonal bars shall be in accordance with Table 3. 2 ISO 2012 All rights reserved ISO 6362-5:2012(E) Table 3 Maximum corner radii Dimensions in millimetres Width across flats b Maximum value of corner radii Square cross-section Hexagonal cro
25、ss-section Alloy group I Alloy group II 10 b 25 1,0 1,5 1,5 25 b 50 1,5 2,0 2,0 50 b 80 2,0 3,0 3,0 80 b 120 2,5 3,0 3,0 120 b 180 2,5 4,0 4,0 180 b 220 3,5 5,0 5,0 5.4 Fixed-length tolerances If fixed lengths are supplied, it shall be agreed between the supplier and purchaser. The permissible toler
26、ances on fixed lengths are given in Table 4. Table 4 Fixed-length tolerance Dimensions in millimetres Diameter or width across flats b Tolerances on fixed lengths L 2 000 2 000 L 5 000 5 000 L 8 000 8 b 100 0 5 + 0 7 + 0 10 + 100 b 200 0 7 + 0 9 + 0 12 + 200 b 350 0 8 + 0 11 + 0 14 + 5.5 Squareness
27、of cut ends The squareness of cut ends shall be within half of the fixed-length tolerance range specified in Table 4 for both fixed and random lengths. For example, for a fixed-length tolerance of 0 10 +mm, the squareness of cut ends shall be within 5 mm. 6 Tolerances on shape 6.1 General The form t
28、olerances specified in 6.2 to 6.4 apply to all tempers, except tempers H112, O and TX510. The deviation shall be measured with the bar supported on a horizontal base-plate, such that the deviation is minimized by the mass of the bar. 6.2 Straightness tolerances The straightness tolerances shall be i
29、n accordance with Table 5. ISO 2012 All rights reserved 3 ISO 6362-5:2012(E) Table 5 Straightness tolerances Dimensions in millimetres Width b Straightness tolerances Per 1 000 mm of total length (l 1 ) h 1 In any 300 mm (l 2 ) h 2 8 b 80 2 0,8 80 b 120 2 1,0 120 b 220 3 1,5 220 b 350 6 3 The deviat
30、ions from straightness h 1and h 2shall be measured as shown in Figure 1, with the bar placed on a horizontal base-plate so that its mass decreases the deviation. Dimensions in millimetres Key 1 base-plate Figure 1 Measurement of deviation from straightness 6.3 Convexity/concavity The convexity/conca
31、vity for bars shall be included within the tolerances on width across flats. 6.4 Twist tolerances Twist tolerances shall be in accordance with Table 6. The twist v shall be measured in accordance with Figure 2. Table 6 Twist tolerances Dimensions in millimetres Width across flats b Twist tolerances
32、v Square cross-section Hexagonal cross-section Per 1 000 mm of length Over the total length Per 1 000 mm of length Over the total length 10 b 30 1 3 1 1,5 30 b 50 1,5 4 1,5 2,5 50 b 120 2 5 2 3 120 b 220 3 6 2,5 4 4 ISO 2012 All rights reserved ISO 6362-5:2012(E) Key b width v measurement position o
33、f twist 1 base-plate Figure 2 Measurement of twist 6.5 Squareness for square bars Squareness tolerances are specified in Table 7. The deviation from square shall be measured as shown in Figure 3. Table 7 Squareness tolerances Dimensions in millimetres Width across flats b Maximum deviation from square z 10 b 100 0,01 b 100 b 180 1,0 180 b 240 1,5 Key Z deviation Figure 3 Measurement of deviation from square (cross-section) ISO 2012 All rights reserved 5ISO 6362-5:2012(E) ISO 2012 All rights reserved ICS 77.150.10 Price based on 5 pages