1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 00 2014 12 15 Released L. Sinclair, NA Controlled document at www.MATS Copyright 2014, Ford Global Technologies, Inc. Page 1 of 3 CARPET, POLYESTER, NON WOVEN, FLAT NEEDLED, WRS-M3H138-A10 LATEX BACKED, MOLDABLE 305 G/M2 (9.0 OZ) NOMINAL
2、FACE 1. SCOPE The materials defined by this specification are flat needled, polyester, non-woven carpets of good quality and uniform composition. This carpet is a solid color matched carpet. 2. APPLICATION This specification was originally released for bin liners and seat back applications, with a s
3、olid color matched face. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS 3.1.1 Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.2 In addition to the requirements listed herein, the end-item carp
4、et assembly shall meet all requirements of the WSS-M8P16-B. 3.1.3 Materials used in interior applications must meet the requirements outlined in WSSM99P2222-D1/ latest for Vehicle Interior Environment Quality Materials/Component Performance Requirements. Test data must to be provided by the Tier 1 a
5、t the appropriate program milestone. 3.1.4 Recycled Content The face material must contain 95% recycled content as defined by WRS-M99P42-A2 (Textile Materials, Identification of Recycled Content). 3.2 SAMPLE SELECTION All evaluations shall be conducted on test specimens taken from finished roll good
6、s prior to any subsequent operations, such as reheating or molding. 3.3 APPEARANCE (FLTM BI 109-01) The color, pattern, and finish shall match the approved Design Center master sample, or shall be as specified on the engineering drawing. 3.4 COMPOSITION (ASTM D 629) 3.4.1 Face Fiber Polyester (95% P
7、CR) ENGINEERING MATERIAL SPECIFICATION WRS-M3H138-A10 Copyright 2014, Ford Global Technologies, Inc. Page 2 of 3 3.4.2 Backing Latex 3.5 METHOD OF DYEING Solution dyed 3.6 CONSTRUCTION 3.6.1 Fiber Size and Description 4.5 denier (ASTM D 1244) 3.6.3 Final Total Thickness 3.2 +/- 0.5 mm (ASTM D 1777)
8、3.7 WEIGHT (FLTM BN 106-01) 3.7.1 Pile Fiber 271 339 g/m2 8.0 10.0 (oz) 3.7.2 Backing 168 204 g/m2 5.0 6.0 (oz) 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Enginee
9、ring Material Specifications. 4.1 DRAWING CALLOUT The following shall be called out on the Engineering drawing to correctly designate the approved material. WRS-M3H138-A10 Supplier Name and Product Code (As it appears on the Approved Source Listing) WSS-M8P16-B 5. SUMMARY OF REVISIONS ENGINEERING MA
10、TERIAL SPECIFICATION WRS-M3H138-A10 Copyright 2014, Ford Global Technologies, Inc. Page 3 of 3 Non Woven Carpet Construction Supplement Supplier _Supplier Contact Name_ Number _ Product/ Style Name _ Material Specification _ Performance Specification _ Supplier Product Code _ Manufacturing Location
11、_ Supplier Lab Number _ Supplier Lab Date _ Composition Type Supplier Face Fiber ASTM D276 _ _ Binder Fiber ASTM D276 _ _ Fabric Backing ASTM D276 _ _ Pre Coat ASTM D276 _ _ Primary Backing ASTM D276 _ _ Secondary Backing ASTM D276 _ _ Construction Solution or piece dyed (circle one) Percent PIR/PRC
12、 _ Denier _ Face Fiber Thickness ISO 1765 _+/- _ mm Binder Fiber Thickness ISO 1765 _+/- _ mm Pre Coating Thickness ISO 1765 _+/- _ mm Primary Thickness ISO 1765 _+/- _ mm Secondary Thickness ISO 1765 _+/- _ mm Mass per Unit Area Weight Face Fiber ASTM D5848 _+/- _ g/m2 Binder Fiber ASTM D5848 _+/- _ g/m2 Pre Coating ASTM D5848 _+/- _ g/m2 Primary Backing ASTM D5848 _+/- _ g/m2 Secondary Backing ASTM D5848 _+/- _ g/m2 Materials Engineering Signature _Date _ Comments _ Rolled Goods _ Molded Product _