1、 International Alloy Designations and Chemical Composition Limits for Wrought Aluminum and Wrought Aluminum Alloys 1525 Wilson Boulevard, Arlington, VA 22209 www.aluminum.org With Support for On-line Access From: Aluminum Extruders Council Australian Aluminium Council Ltd. European Aluminium Associa
2、tion Japan Aluminium Association Alro S.A, Romania Revised: January 2015 Supersedes: February 2009 Copyright 2015, The Aluminum Association, Inc. Unauthorized reproduction and sale by photocopy or any other method is illegal. Use of the Information The Aluminum Association has used its best efforts
3、in compiling the information contained in this publication. Although the Association believes that its compilation procedures are reliable, it does not warrant, either expressly or impliedly, the accuracy or completeness of this information. The Aluminum Association assumes no responsibility or liab
4、ility for the use of the information herein. All Aluminum Association published standards, data, specifications and other material are reviewed at least every five years and revised, reaffirmed or withdrawn. Users are advised to contact The Aluminum Association to ascertain whether the information i
5、n this publication has been superseded in the interim between publication and proposed use. CONTENTS Page FOREWORD . i SIGNATORIES TO THE DECLARATION OF ACCORD . ii-iii REGISTERED DESIGNATIONS AND CHEMICAL COMPOSITION LIMITS 1-14Footnotes 15 TABLE OF NOMINAL DENSITIES FOR ACTIVE ALLOYS . 16-21 TABLE
6、 OF INACTIVE ALLOY DESIGNATIONS . 22-23 Table of Chemical Composition Limits for Inactive Original Alloys . 24-26 CROSS REFERENCES OF INTERNATIONAL DESIGNATIONS DECLARATION OF ACCORD (DOA) TO ISO . 27 RECOMMENDATION TO THE DECLARATION OF ACCORD 28 Footnotes 29 Appendix AUse and Assignment of Designa
7、tions . 30 Appendix BDeactivation of Registered Alloys . 30 Appendix CGeneral Guidelines for Determining Compliance with “Sale of Alloy“ and “Commercial Quantity“ for Purposes of Registering Wrought Aluminum and Wrought Aluminum Alloys . 30 DECLARATION OF ACCORD 31 i FOREWORD Listed herein are desig
8、nations and chemical composition limits for wrought aluminum and wrought aluminum alloys registered with The Aluminum Association. Numerical designations are assigned in accordance with the RecommendationInternational Designation System for Wrought Aluminum and Wrought Aluminum Alloys, which is prin
9、ted on pages 28 through 30. Additions may be made in accordance with the rules outlined in the Declaration of Accord printed on page 31, and alloys will be deleted when no longer in commercial use (see table of inactive alloys printed on pages 22-23). Since the International Designation System for W
10、rought Aluminum and Wrought Aluminum Alloys is based on USAs national standard “American National Standard Alloy and Temper Designation System for Aluminum ANSI H35.1,“ the system limits introduction of experimental alloy compositions to USA registrations. An experimental alloy registered by USA und
11、er this system is indicated by the prefix “X“ and is subject to the following rules: 1. A composition shall not be designated as experimental (“X“) for more than five years. 2. During its experimental status, the registering organization may request changes in the composition limit of the alloy, pro
12、vided that it does not invalidate any assigned designation. 3. The “X“ is dropped when the alloy is no longer experimental. 4. An experimental composition that is inactivated shall retain the prefix “X“ for the duration of its inactive status. If reactivated, the “X“ shall be removed. Some of the re
13、gistered alloys may be the subject of patent or patent applications, and their listing herein is not to be construed in any way as the granting of a license under such patent right. This registration record is not intended to address all regulatory requirements that may be imposed by local, national
14、 or international governing bodies. Regulatory requirements, which vary by region and end use, can further restrict the chemical composition within the registered limits. When applicable, inclusion of such requirements in the sales agreement is advised. A list of the organizations that are signatori
15、es to the Declaration of Accord on the Recommendation is printed on pages ii-iii. ii SIGNATORIES TO THE DECLARATION OF ACCORD The following organizations are signatories to the Declaration of Accord on an International Alloy Designation System for Wrought Aluminum and Wrought Aluminum Alloys which i
16、s printed on page 31 of this publication. The Aluminum Association Inc. USA 1525 Wilson Boulevard Suite 600 Arlington, VA 22209 USA www.aluminum.org AFA Association Francaise de lAluminium FRANCE 17, rue de lamiral Hamelin 75783 Paris Cedex 16 FRANCE www.aluminium- All-Russian Institute of Aviation
17、Materials (VIAM) RUSSIA 17 Radio Ulitza 105005 Moscow RUSSIA www.viam.ru Alro S.A. ROMANIA 116 Pitesti Street Slatina, Olt County 230048 ROMANIA www.alro.ro Aluminium Association of Canada CANADA 1010 Sherbrooke Street West, Suite 1600 Montreal, Quebec H3A 2R7 CANADA www.aac.aluminium.qc.ca Aluminiu
18、m Center Belgium BELGIUM Z.I. Research Park 310 B-1731 Zellik BELGIUM www.aluminiumcenter.be Aluminium Federation Limited UK National Metalforming Centre 47 Birmingham Road West Bromwich, West Midlands B70 6PY UNITED KINGDOM www.alfed.org.uk Aluminium Federation of South Africa SOUTH AFRICA P. O. Bo
19、x 423 Isando, 1600 REPUBLIC OF SOUTH AFRICA www.afsa.org.za Aluminium Verband Schweiz SWITZERLAND Hallenstrasse 15 Postfach 71 CH-8024 Zurich SWITZERLAND www.alu.ch Associaco Brasileira do AluminioABAL BRAZIL Rua HumbertoI, n 220 - 4 .Andar Vila Mariana - CEP: 04018-030 Sao Pulo-SP BRAZIL www.abal.o
20、rg.br Association for the Dutch NETHERLANDS Metallurgic Industry (VNMI) P.O. Box 190 NL-2700 AD Zoetermeer NETHERLANDS www.vnmi.nl Assomet - Associazione Nazionale ITALY Industrie Metalli non Ferrosi Via dei Missaglia, 97 I-20142 Milano ITALY www.assomet.it Australian Aluminium Council Limited AUSTR
21、ALIA Level 1, Dickson Square P.O. Box 63 Dickson, Canberra ACT 2602 AUSTRALIA www.aluminium.org.au Austrian Non-Ferrous Metals Federation AUSTRIA Wiedner Hauptstrae 63 1045 Vienna AUSTRIA www.nemetall.at Centro Nacional de Investigaciones SPAIN Metalurgicas (CENIM) Avenida Gregorio del Amo, 8 Ciudad
22、 Universitaria 28040 Madrid SPAIN www.cenim.csic.es China Nonferrous Metals Techno-Economic CHINA Research Institute No. 31 Suzhou Street Haidian District Bejing, 100080 PEOPLES REPUBLIC OF CHINA European Aluminium Association EAA Avenue de Broqueville, 12 B-1150 Brussels BELGIUM www.aluminium.org
23、Signatories (Continued) iii European Organization for ASD-STAN Aerospace Standardization Rue Montoyer 10/5 1000 Brussels BELGIUM www.asd-stan.org Gesamtverband der Aluminium- GERMANY industrie e.V. (GDA) Am Bonneshof 5 D-40474 Dusseldorf GERMANY www.aluinfo.de Institute of Non-Ferrous Metals POLAND
24、Light Metals Divison ul. Pilsudskiego 19 32-050 Skawina POLAND www.imn.gliwice.pl Instituto Mexicano del Alumino, A.C. MEXICO Francisco Petrarca No. 133 Piso 9 MEXICO, D.F. 11560 www.imedal.org.mx IRAM-Instituto Argentino De ARGENTINA Normalizacion Peru 552/6 C1068AAB Buenos Aires ARGENTINA www.iram
25、.org.ar Japan Aluminium Association JAPAN Tsukamoto-Sozan Building 2-15, Ginza 4-Chome Chuo-ku, Tokyo 104-0061 JAPAN www.aluminum.or.jp The Swedish Aluminium Association SWEDEN Svenskt Aluminium Romfartuna Nortuna 1 SE-725 94 Vsters SWEDEN www.svensktaluminium.se CHEMICAL COMPOSITION LIMITS1, 2 Only
26、 composition limits which are identical to those listed herein for a registered designation are applicable to that designation. See footnotes on page 15. 1 NATURAL IMPURITY LIMITS FOR WROUGHT UNALLOYED ALUMINUM Registered International Designation OTHERS13 Al No. 17 Date By Si Fe Cu Mn Mg Cr Ni Zn T
27、i Ag B Bi Ga Li Pb Sn V Zr Each Total3 Minimum1050 1954 USA 0.25 0.40 0.05 0.05 0.05 elipsis elipsis 0.05 0.03 elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.05 elipsis elipsis 0.03 elipsis 99.50 4 1050A 1972 EAA 0.25 0.40 0.05 0.05 0.05 elipsis elipsis 0.07 0.05 elipsis elipsis elipsis e
28、lipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.03 elipsis 99.50 4 1060 1954 USA 0.25 0.35 0.05 0.03 0.03 elipsis elipsis 0.05 0.03 elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.05 elipsis elipsis 0.03 elipsis 99.60 4 1065 1973 USA 0.25 0.30 0.05 0.03 0.03 elipsis elipsis 0.05 0
29、.03 elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.05 elipsis elipsis 0.03 elipsis 99.65 4 1070 1954 USA 0.20 0.25 0.04 0.03 0.03 elipsis elipsis 0.04 0.03 elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.05 elipsis 6 0.03 elipsis 99.70 4 1070A 1972 EAA 0.20 0.25 0.03 0.03 0.03 e
30、lipsis elipsis 0.07 0.03 elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.03 elipsis 99.70 4 1080 1954 USA 0.15 0.15 0.03 0.02 0.02 elipsis elipsis 0.03 0.03 elipsis elipsis elipsis 0.03 elipsis elipsis elipsis 0.05 elipsis elipsis 0.02 elipsis 99.80 4 1080A 1972 EAA
31、 0.15 0.15 0.03 0.02 0.02 elipsis elipsis 0.06 0.02 elipsis elipsis elipsis 0.03 elipsis elipsis elipsis elipsis elipsis 6 0.02 elipsis 99.80 4 1085 1954 USA 0.10 0.12 0.03 0.02 0.02 elipsis elipsis 0.03 0.02 elipsis elipsis elipsis 0.03 elipsis elipsis elipsis 0.05 elipsis elipsis 0.01 elipsis 99.8
32、5 4 1090 1954 USA 0.07 0.07 0.02 0.01 0.01 elipsis elipsis 0.03 0.01 elipsis elipsis elipsis 0.03 elipsis elipsis elipsis 0.05 elipsis elipsis 0.01 elipsis 99.90 4 1098 1972 GERMANY 0.010 0.006 0.003 elipsis elipsis elipsis elipsis 0.015 0.003 elipsis elipsis elipsis elipsis elipsis elipsis elipsis
33、elipsis elipsis elipsis 0.003 elipsis 99.98 5 REGISTERED COMPOSITIONS Registered International Designation OTHERS13 Al No. 17 Date By Si Fe Cu Mn Mg Cr Ni Zn Ti Ag B Bi Ga Li Pb Sn V Zr Each Total3 Minimum 1100 1954 USA elipsis elipsis 0.05-0.20 0.05 elipsis elipsis elipsis 0.10 elipsis elipsis elip
34、sis elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.95 Si+Fe 6 0.05 0.15 99.00 4 1100A 2005 JAPAN elipsis elipsis 0.05-0.20 0.05 0.10 elipsis elipsis 0.10 0.10 elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis 1.00 Si+Fe 0.05 0.15 99.00 4 1200 1966 USA elipsis elipsis
35、 0.05 0.05 elipsis elipsis elipsis 0.10 0.05 elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis 1.00 Si+Fe6 0.05 0.15 99.00 4 1200A 1991 NORWAY elipsis elipsis 0.10 0.30 0.30 0.10 elipsis 0.10 elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis 1.00 S
36、i+Fe 0.05 0.15 99.00 4 130015 2000 FRANCE 0.20 0.30 0.05 0.03 0.03 elipsis elipsis 0.20-0.50 0.03 elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.05 0.15 99.00 4 1110 1987 FRANCE 0.30 0.8 0.04 0.01 0.25 0.01 elipsis elipsis elipsis elipsis 0.02 elipsis elipsis elips
37、is elipsis elipsis elipsis elipsis 0.03 V+Ti 0.03 elipsis 99.10 4 1120 1982 AUSTRALIA 0.10 0.40 0.05-0.35 0.01 0.20 0.01 elipsis 0.05 elipsis elipsis 0.05 elipsis 0.03 elipsis elipsis elipsis elipsis elipsis 0.02 V+Ti 0.03 0.10 99.20 4 123015 1954 USA elipsis elipsis 0.10 0.05 0.05 elipsis elipsis 0
38、.10 0.03 elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.05 elipsis 0.70 Si+Fe 0.03 elipsis 99.30 4 1230A 2005 JAPAN elipsis elipsis 0.10 0.05 0.05 elipsis elipsis 0.05 elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.70 Si+Fe 0.03 elipsis 99.30 4 1235 1954
39、 USA elipsis elipsis 0.05 0.05 0.05 elipsis elipsis 0.10 0.06 elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.05 elipsis 0.65 Si+Fe 0.03 elipsis 99.35 4 1435 1958 USA 0.15 0.30-0.50 0.02 0.05 0.05 elipsis elipsis 0.10 0.03 elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.05 elipsi
40、s elipsis 0.03 elipsis 99.35 4 1145 1954 USA elipsis elipsis 0.05 0.05 0.05 elipsis elipsis 0.05 0.03 elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.05 elipsis 0.55 Si+Fe 0.03 elipsis 99.45 4 1345 1956 USA 0.30 0.40 0.10 0.05 0.05 elipsis elipsis 0.05 0.03 elipsis elipsis elipsis elipsis
41、elipsis elipsis elipsis 0.05 elipsis elipsis 0.03 elipsis 99.45 4 + 1445 1973 AUSTRALIA elipsis elipsis 0.04 elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.50 Si+Fe+Cu elipsis 0.05 99.45 4 1150 1973 AUSTRALIA elipsis elipsis
42、0.05-0.20 0.05 0.05 elipsis elipsis 0.05 0.03 elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.45 Si+Fe 0.03 elipsis 99.50 4 135011 1975 USA 0.10 0.40 0.05 0.01 elipsis 0.01 elipsis 0.05 elipsis elipsis 0.05 elipsis 0.03 elipsis elipsis elipsis elipsis elipsis 0.02 V+Ti 0.03
43、 0.10 99.50 4 1350A 1979 GERMANY 0.25 0.40 0.02 elipsis 0.05 elipsis elipsis 0.05 elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.03 Cr+Mn+Ti+V 0.03 elipsis 99.50 4 1450 1990 EAA 0.25 0.40 0.05 0.05 0.05 elipsis elipsis 0.07 0.10-0.20 elipsis elipsis elipsis elipsis
44、 elipsis elipsis elipsis elipsis elipsis 6 0.03 elipsis 99.50 4 1370 1976 FRANCE 0.10 0.25 0.02 0.01 0.02 0.01 elipsis 0.04 elipsis elipsis 0.02 elipsis 0.03 elipsis elipsis elipsis elipsis elipsis 0.02 V+Ti 0.02 0.10 99.70 4 1275 1986 SPAIN 0.08 0.12 0.05-0.10 0.02 0.02 elipsis elipsis 0.03 0.02 el
45、ipsis elipsis elipsis 0.03 elipsis elipsis elipsis 0.03 elipsis elipsis 0.01 elipsis 99.75 4 CHEMICAL COMPOSITION LIMITS1, 2 REGISTERED COMPOSITIONContinued Only composition limits which are identical to those listed herein for a registered designation are applicable to that designation. See footnot
46、es on page 15. 2 Registered International Designation OTHERS13 Al No. 17 Date By Si Fe Cu Mn Mg Cr Ni Zn Ti Ag B Bi Ga Li Pb Sn V Zr Each Total3 Minimum 1185 1954 USA elipsis elipsis 0.01 0.02 0.02 elipsis elipsis 0.03 0.02 elipsis elipsis elipsis 0.03 elipsis elipsis elipsis 0.05 elipsis 0.15 Si+Fe
47、 0.01 elipsis 99.85 4 1285 1954 USA 0.08 0.08 0.02 0.01 0.01 elipsis elipsis 0.03 0.02 elipsis elipsis elipsis 0.03 elipsis elipsis elipsis 0.05 elipsis 0.14 Si+Fe 0.01 elipsis 99.85 4 1385 1987 FRANCE 0.05 0.12 0.02 0.01 0.02 0.01 elipsis 0.03 elipsis elipsis 0.02 elipsis 0.03 elipsis elipsis elips
48、is elipsis elipsis 0.03 V+Ti 0.01 elipsis 99.85 4 1188 1954 USA 0.06 0.06 0.005 0.01 0.01 elipsis elipsis 0.03 0.01 elipsis elipsis elipsis 0.03 elipsis elipsis elipsis 0.05 elipsis 6 0.01 elipsis 99.88 4 1190 1987 FRANCE 0.05 0.07 0.01 0.01 0.01 0.01 elipsis 0.02 elipsis elipsis 0.01 elipsis 0.02 e
49、lipsis elipsis elipsis elipsis elipsis 0.01 V+Ti 0.01 elipsis 99.90 4 1290 2005 JAPAN 0.050 0.030 0.050 elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis elipsis 0.01 elipsis 99.90 5 1193 1964 USA 0.04 0.04 0.006 0.01 0.01 elipsis elipsis 0.03 0.01 elipsis elipsis elipsis 0.03 elipsis elipsis elipsis 0.05 elipsis elipsi