1、Designation: D4287 00 (Reapproved 2010)Standard Test Method forHigh-Shear Viscosity Using a Cone/Plate Viscometer1This standard is issued under the fixed designation D4287; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year o
2、f last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This test method covers the determi
3、nation of the viscos-ity of paints, varnishes, and related products at a rate of shearof 12 000 s1.1.2 Paints and varnishes that dry very rapidly may not givereproducible results with this test method. Measurements madeat elevated temperatures may also give poor precision due toloss of volatiles and
4、 to drying.1.3 The values stated in SI units are to be regarded asstandard. No other units of measurement are included in thisstandard.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to est
5、ablish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D1210 Test Method for Fineness of Dispersion of Pigment-Vehicle Systems by Hegman-Type GageD3925 Practice for Sampling Liquid Paints and
6、RelatedPigmented CoatingsD4958 Test Method for Comparison of the Brush Drag ofLatex Paints3. Summary of Test Method3.1 The material to be tested is placed between the cone andplate of a cone/plate viscometer, then subjected to a high shearrate while the viscosity is determined.4. Significance and Us
7、e4.1 The viscosity value obtained by this test method givesinformation about the flow properties of the material underhigh-shear conditions similar to those encountered duringapplication: brushing (see Test Method D4958), spraying,electrostatic disk, or roll coating.4.2 This test method is suitable
8、for all paints and varnisheswhether they are Newtonian in behavior or not. However, dueto the narrow gap between the stationary and rotary parts ofhigh-shear viscometers, this test method is more reproduciblefor paints having finer pigment dispersions as determined byTest Method D1210.5. Apparatus5.
9、1 Cone/Plate Type Viscometer,with cone/speed combina-tion producing a rate of shear of 12 000 s1. The viscometermust provide a viscosity measurement rage of either 0 to 10 (P)or 0 to 5 (P) at the above mentioned shear rate. With higherviscosity materials, other cones and speeds may be used uponagree
10、ment between the producer and the user, but it should benoted that these may give lower shear rates not truly represen-tative of application conditions. Refer to Fig. 1 and Fig. 2 of ananalog and digital cone and plate viscometer.NOTE 1The SI units for viscosity are pascal-seconds (Pas = 10 P, 1mPas
11、 = 1 cP).6. Reagents and Materials6.1 Water or SolventThe viscometer should be zeroedaccording to the manufacturers specification. Zeroing proce-dures that require liquid may be satisfied with water or a lowviscosity solvent such as xylene or mineral spirits.6.2 Mineral OilsThree standard mineral oi
12、ls with knownviscosities (certified by an approved laboratory) lying between10 and 90 % of full scale to be used for calibrating theinstrument.3NOTE 2Silicone oils should be avoided because of their tendency tocontaminate instruments, containers and other equipment and because ofthe possibility of s
13、hear thinning behavior at high shear rates.7. Sampling7.1 Take a representative sample of the product to be testedin accordance with Practice D3925. If the sample has atendency to settle or separate on standing, it must be stirred or1This test method is under the jurisdiction of ASTM Committee D01 o
14、n Paintand Related Coatings, Materials, and Applications and is the direct responsibility ofSubcommittee D01.24 on Physical Properties of Liquid Paints and Paint Materials.Current edition approved Feb. 1, 2010. Published February 2010. Originallyapproved in 1983. Last previous edition approved in 20
15、05 as D4287 00 (2005).DOI: 10.1520/D4287-00R10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Such oils are
16、 available from The Cannon Instrument Co., P.O. Box 16, StateCollege, PA 16801.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.shaken until homogeneous before a test specimen is taken fromit. The specimen must be free of any foreign
17、matter or airbubbles and its volume must be sufficient to cover the portionof the viscometer plate under the cone when the latter isbrought into contact with the plate.8. Preparation of Apparatus8.1 The viscometer should be zeroed on a daily basis whenin regular use or otherwise before use, accordin
18、g to theviscometer operating manual. With the analog-type viscometer,if the pointer does not indicate zero, it may be adjusted bymeans of a lever on the left-hand side of the upper part of theinstrument housing. If the instrument cannot be zeroed, adjust-ment should take place according to the manuf
19、acturers sug-gestions.8.2 Verify the calibration of the apparatus by following theprocedure in Section 9, but using standard refined mineral oilshaving Newtonian characteristics and known viscosities. If theviscometer reads the correct viscosity (or within 5 % of thatvalue) with two or more oils who
20、se viscosities bracket those ofspecimens to be tested, then the viscometer readings may beused as is. If the viscometer readings do not give the correctviscosities for the oils, then a calibration curve must beconstructed by taking viscometer readings for three oils andplotting measured viscosity ve
21、rsus specified (correct) viscosityfor the oils. Subsequent measurements are corrected to trueviscosities through use of the curve.8.3 Check the cones periodically for wear. Replace any conethat shows a definite flattening of the apex. Some users havefound it necessary to replace cones every year. Ot
22、hers have hadto do so more often when abrasive paints or pastes were beingtested.8.4 The determination must be made at a closely controlledtemperature of 25 6 0.3C, unless otherwise agreed. In orderto check the temperature control, carry out the test as outlinedin 9.1 with the standard refined miner
23、al oil of the highestviscosity. Allow the viscometer to run with this oil for 5 minand determine whether the reading decreases. If the decrease ismore than 10 %, the apparatus is unsuitable for the determina-tion of viscosities at high rates of shear in accordance with thistest method.NOTE 3Many mul
24、titemperature cone/plate viscometers have heating,but not cooling, capabilities. Therefore, runs with these viscometers at25C should only be done at room temperatures at or below 22C toensure that the plate temperature does not go above 25C.9. Procedure9.1 With the cone in the down position (in cont
25、act with theplate), turn the instrument on and allow it to warm up for atleast 5 min. For a multitemperature instrument, set at 25C orto an alternatively agreed upon temperature. Raise the cone tothe up position. Transfer a suitable amount of the product to beFIG. 1 Analog Cone and Plate ViscometerF
26、IG. 2 Digital Cone and Plate ViscometerD4287 00 (2010)2tested to the plate, taking care to avoid the inclusion of airbubbles, and again lower the cone to the down position. Waitfor 30 s to allow the specimen to attain the agreed upontemperature.9.2 Start the cone rotating and record the reading. Whe
27、nusing an analog viscometer, record the reading when the pointbecomes steady (Note 4). When using a digital viscometer,record the reading directly from the digital display once it hasbeen stabilized (Note 5).NOTE 4With an analog cone/plate viscometer, whether the readinggives a direct indication of
28、the viscosity or not, depends on the cone andscale used.NOTE 5In some cases it is difficult to judge whether a constantreading has been obtained. However, if the reading does not becomesteady after 15 s, record the reading at 15 s and mention the lack of aconstant reading in the test report. If high
29、ly accurate readings are required,make the readings below 90 % of the scale.9.3 If the reading does not directly indicate the viscosity,multiply the reading by the appropriate conversion factor oruse the appropriate calibration curve to obtain the viscosity.9.4 Clean both the cone and the plate care
30、fully, employinga cloth or tissue and a suitable solvent. Take care to remove allof the test material and cleaning solvent. Do not use cleaningutensils that may damage the apparatus. Metal cleaning toolsmust never be used.9.5 Repeat the determination with a second specimen. If thetwo viscosity deter
31、minations differ by less than 7 %, calculatetheir mean and report as the high-shear viscosity for thematerial. If they differ by more than 7 %, make a thirddetermination. If no two readings are within 7 % of each other,then the material is not suitable for testing by this test method.10. Report10.1
32、Report the following information:10.1.1 Reference to this test method and the viscometerused,10.1.2 Type and identification of the product under test,10.1.3 Type of cone used,10.1.4 Rate of shear at which the determination was made(in reciprocal seconds),10.1.5 Temperature at which the determination
33、 was made,10.1.6 Test results in poises, reported to the nearest 1 % ofthe total range, that is, 0.05 P for 0 to 5 P-cones, 0.1 P for 0 to10 P-cones, etc.,10.1.7 Any deviation, by agreement or otherwise, from thetest procedures described, and10.1.8 Date of the test.11. Precision and Bias411.1 Precis
34、ionOn the basis of an interlaboratory test ofthis test method in which eight operators in four laboratoriestested six paints ranging in viscosity from 0.8 to 7.9 P onanalog cone/plate viscometers, the within-laboratory coeffi-cient of variation was found to be 2.2 %, at 40 df. Thebetween-laboratory
35、coefficient of variation was found to be6.9 % at 34 df. Based on these results, the following criteriashould be used for judging the acceptability of results at the95 % confidence level:11.1.1 RepeatabilityTwo test results, each the mean oftwo determinations, obtained by the same operator should bec
36、onsidered suspect if they differ by more than 6.3 % relative.11.1.2 ReproducibilityTwo results, each the mean of twodeterminations, obtained by operators in different laboratoriesshould be considered suspect if they differ by more than 19.9 %relative.11.2 BiasSince there is no accepted reference mat
37、erialsuitable for determining the bias for the procedure in this testmethod, bias has not been determined.12. Keywords12.1 viscositypaints/related coatings/materials; viscom-eterICI cone/plate; viscometercone/plateASTM International takes no position respecting the validity of any patent rights asse
38、rted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by
39、 the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will recei
40、ve careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM Inter
41、national, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).4Supporting data have been filed at ASTM International Headquarters and maybe obtained by requesting Research Report RR:D01-1035.D4287 00 (2010)3