1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions Rev. 02012 04 04 Activated M. Montgomery, EU Controlled document at www.MATS Copyright 2012, Ford Global Technologies, LLC Page 1 of 2 FABRIC, ECKO PATTERN, WOVEN DOBBY, WSS-M1H1070-A LAMINATED-TEXTAB 1. SCOPE The material defined by this spec
2、ification is a woven dobby polyester face fabric; Laminated and finished with Textab (HF-welded PVC). 2. APPLICATION This specification was released originally for material used as an interior trim fabric for use in the V36x 2013 Model Year. 3. REQUIREMENTS In addition to the requirements listed her
3、ein, the fabric and PVC combination shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable; 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.2 FABRIC CO
4、NSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D3775) Warp 218/10 cm Weft 176/10 cm 3.2.2 Fabric Weight, +/- 10% tolerance (FLTM BN 106-01) 340 g/m2 3.2.3 Total weight, +/- 10% tolerance 780 g/m2(Including lamination and welded vinyl stripes) 3.3 COMPOSITION (ASTM D629) Fabric 100 % polyester
5、 Welded Stripes 100 % PVC film ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1070-ACopyright 2012, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D1244) Warp 830dtex; f192, Polyester, air textured, round, semi dull solution dyed Weft 830dtex; f192, Polyester, air textured, round, s
6、emi dull, spun-dyed 550dtex; f108, Polyester, Fully oriented, trilobal, bright, spun-dyed 3.5 METHOD OF DYEING Spun dyed or as approved by Materials Engineering 3.6 FINISHED OPERATIONS Washing Tenter frame Foam lamination- HF welding PVC 3.7 PVC Type: A6640 Weight: 900 +/-70 g/m Thickness: 750 +/-50
7、 mym 10 mm wide, PVC stripes, welded to face fabric 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 Purchase departments will
8、ensure that the material defined in this specification and shipped to any one assembly plant will be produced by one supplier only. 4.2 Global cross car line strategies to use tri-laminate construction in all regions. 4.3 If yarn is locally sourced it must meet the above fabric construction, Composition & Yarn Construction. The fabric must also meet the requirements of WSS-M8P18-A1/A2/A3/A4.