1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 02 03 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 2 FABRIC, MUSTANG PATTERN, FLAT WOVEN WSS-M1H964-A 1. SCOPE The material defined by this specification is a MUSTANG patt
2、ern, Jacquard flat woven bodycloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an insert of seat fabric for the 2004 S197 Mustang seats. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet al
3、l requirements of: WSS-M8P18-A1/A4. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3775) Warp 4
4、72 ends/10 cm Fill 228 picks/10 cm 3.2.2 Fabric Weight, range (FLTM BN 106-01) Face Fabric w/backcoat 234 - 259 g/m2Laminated to 3mm foam 376 415 g/m23.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4. Fabric 100% Semi-Dull Polyester Backcoating EVA ENGINEERING MATERIAL SPECIFICA
5、TIONWSS-M1H964-A Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 16.7tex f34 (false twist semi-dull round polyester) Fill 27.8tex f100(false twist semi-dull round polyester) x 2 3.5 METHOD OF DYEING Piece Dye, Disperse Dye 3.6 FINISHING OPERATIONS Set Make, wash, jet scour, dye, scotch, dry, coat