1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 07 27 Activated N. J. Komatsu Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 2 FABRIC, PIEGA PATTERN, WOVEN JACQUARD, WSS-M1H1000-A UNLAMINATED 1. SCOPE The material defined by this specification i
2、s a woven jacquard polyester face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for use in the S389. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as appl
3、icable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 10% tolerance (ASTM D 3775) Warp 275 ends/10 cm Weft 170 pick
4、s/10 cm 3.2.2 Fabric Weight, +/- 15% tolerance (FLTM BN 106-01) 238-322 g/m23.3 COMPOSITION (ASTM D 629) Fabric 100% polyester 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 520-580 dtex f129-158 (air texturized, semi-dull) Weft 530-590 dtex f129-158 (air texturized, bright) ENGINEERING MATERIAL SPECIFICA
5、TIONWSS-M1H1000-APrinted copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 2 of 2 3.5 METHOD OF DYEING Yarn dyed or as approved by Materials Engineering 3.6 FINISHED OPERATIONS As approved by Materials Engineering 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.